Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | Saturation, 23°C | ISO 62 | 7.0 | % |
| Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | 2.0 | % |
| Melt Volume flow Rate | 275°C/5.0 kg | ISO 1133 | 100 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ISO 527-2 | 3000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Glass Transition Temperature | | ISO 11357-2 | 125 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Tearing Strength | MD | ISO 6383-1 | 5.00 | N/mm |
| Tearing Strength | TD | ISO 6383-1 | 5.00 | N/mm |
| Carbon Dioxide Transmission Rate | 23°C 2 | ASTM D256A | 90.0 | cm³/m²/bar/24 hr |
| Carbon Dioxide Transmission Rate | 23°C 3 | ASTM D256A | 40.0 | cm³/m²/bar/24 hr |
| Water Vapor Transmission Rate | 23°C, 85% RH | DIS 15106-1/-2 | 7.0 | g/m²/24 hr |
| Tensile Stress | MD : Yield | ISO 527-3 | 85.0 | Mpa |
| Tensile Stress | TD : Yield | ISO 527-3 | 85.0 | Mpa |
| Tensile Stress | MD : Break | ISO 527-3 | 80.0 | Mpa |
| Tensile Elongation | MD : Yield | ISO 527-3 | 5.0 | % |
| Tensile Elongation | TD : Yield | ISO 527-3 | 5.0 | % |
| Tensile Elongation | MD : Break | ISO 527-3 | 200 | % |
| Tensile Elongation | TD : Break | ISO 527-3 | 200 | % |
| Elmendorf Tear Strength | MD | ISO 6383-2 | 10 | N |
| Elmendorf Tear Strength | TD | ISO 6383-2 | 10 | N |
| Oxygen Transmission Rate | 23°C 2 | ASTM D256A | 30 | cm³/m²/bar/24 hr |
| Oxygen Transmission Rate | 23°C 3 | ASTM D256A | 10 | cm³/m²/bar/24 hr |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| ISO Type | | ISO 1874 | PA 6I/6T, FT, 09-030 | |
| Gloss | 60° | ISO 2813 | 160 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.