PPA AMODEL® A-6135 HN BK324 SOLVAY USA

Unit Price:
$5657 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
23MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD	ASTMD955	0.60	%
	Modeling Shrinkage	TD	ASTMD955	0.90	%
		Modeling Shrinkage	TD	ISO294-4	1.0	%
		Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	0.50	%
Moisture Absorption	24hr	ASTMD570	0.30	%
Moisture Absorption	Moisture Absorption	23°C,24hr	ISO62	0.29	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Break,23°C	ISO527-2	211	Mpa
	Tensile Stress	Break,24°C	ISO527-2	121	Mpa
		Tensile Stress	Break,150°C	ISO527-2	92.4	Mpa
		Tensile Stress	Tensile Stress	Break,175°C	ISO527-2	82.0	Mpa
Tensile Strain	Break,150°C	ISO527-2	4.9	%
	Tensile Strain	Break,175°C	ISO527-2	4.7	%
		Tensile Strain	Break,23°C	ISO527-2	2.0	%
		Tensile Strain	Tensile Strain	Break,24°C	ISO527-2	4.3	%
Tensile Modulus		ASTMD638	13800	Mpa
	Tensile Modulus	23°C	ISO527-2	11500	Mpa
		Tensile Modulus	100°C	ISO527-2	7310	Mpa
			Tensile Modulus	150°C	ISO527-2	6270	Mpa
			Tensile Modulus	Tensile Modulus	175°C	ISO527-2	5310	Mpa
Tensile Elongation	Break	ASTMD638	1.9	%
Flexural Modulus		ASTMD790	11400	Mpa
	Flexural Modulus	23°C	ISO178	11400	Mpa
		Flexural Modulus	100°C	ISO178	6600	Mpa
			Flexural Modulus	150°C	ISO178	4900	Mpa
			Flexural Modulus	Flexural Modulus	175°C	ISO178	4600	Mpa
Flexural Strength		ASTMD790	310	Mpa
Flexural Stress	3.5%Strain,150°C	ISO178	123	Mpa
	Flexural Stress	3.5%Strain,175°C	ISO178	112	Mpa
		Flexural Stress	3.5%Strain,23°C	ISO178	300	Mpa
		Flexural Stress	Flexural Stress	3.5%Strain,100°C	ISO178	170	Mpa
Compressive Strength		ASTMD695	148	Mpa
Shearing Strength		ASTMD732	87.6	Mpa
Poisson Ratio		7.58	0.39
Tensile Strength		ASTMD638	203	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	TD：100to200°C	ASTME831	1E-04	cm/cm/°C
	Linear thermal expansion coefficient	MD：0to100°C	ASTME831	2.2E-05	cm/cm/°C
		Linear thermal expansion coefficient	MD：100to200°C	ASTME831	1.6E-05	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：0to100°C	ASTME831	6.1E-05	cm/cm/°C
Melting temperature		ISO11357-3	310	°C
Melting temperature	Melting temperature		ASTMD570	310	°C
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	303	°C
	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	288	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Annealed,3.20mm	ASTMD648	291	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23°C	ISO179/1eU	60	kJ/m²
Notched Izod impact strength	23°C	ISO180	62	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTMD785	125

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.