PETG 0601 EASTMAN USA
187
- Unit Price:
- $2430 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 195MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High transparency High toughness
- Application Areas:packing sporting goods
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23°C,24hr | ASTMD570,ISO62 | 0.13 | % |
| Intrinsic viscosity 2 | Film:23°C | 内部方法 | 0.70 | |
| Pellets:23°C | 内部方法 | 0.75 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield,23°C | ASTMD638,ISO527-2 | 50.0 | Mpa |
| Break,23°C | ASTMD638,ISO527-2 | 28.0 | Mpa | |
| Bending stress | 23°C | ISO178 | 68.0 | Mpa |
| Yield,23°C | ASTMD790 | 70.0 | Mpa | |
| Tear resistance | M.D.:23°C | 93 | N | |
| T.D.:23°C | 93 | N | ||
| Tensile modulus | 23°C | ASTMD638,ISO527-2 | 2100 | Mpa |
| elongation | Break,23°C | ASTMD638 | 130 | % |
| Break,23°C | ISO527-2 | 100 | % | |
| Bending modulus | 23°C | ASTMD790 | 2100 | Mpa |
| 23°C | ISO178 | 2000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 70.0 | °C |
| 1.8MPa,Unannealed | ASTMD648 | 64.0 | °C | |
| Glass transition temperature | DSC | 80.0 | °C | |
| specific heat | 60°C | DSC | 1300 | J/kg/°C |
| 100°C | DSC | 1760 | J/kg/°C | |
| 150°C | DSC | 1880 | J/kg/°C | |
| 200°C | DSC | 1970 | J/kg/°C | |
| 250°C | DSC | 2050 | J/kg/°C | |
| thermal conductivity | 23°C | ASTMC177 | 0.21 | W/m/K |
| Linear coefficient of thermal expansion | MD：-30to40°C | ASTMD696 | 5.1E-05 | cm/cm/°C |
| Vicat softening temperature | ASTMD1525 | 85.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 23°C,1kHz | ASTMD150 | 5E-03 | |
| 23°C,1MHz | ASTMD150 | 0.020 | ||
| Dielectric strength 10 | 23°C | ASTMD149 | 16 | KV/mm |
| Surface resistivity | ASTMD257 | 1E+16 | ohms | |
| Dielectric constant | 23°C,1kHz | ASTMD150 | 2.60 | |
| 23°C,1MHz | ASTMD150 | 2.40 | ||
| Arc resistance | ASTMD495 | 158 | sec | |
| Volume resistivity | 23°C | ASTMD257 | 1E+15 | ohms·cm |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film thickness - tested | 250 | µm | ||
| Oxygen permeability rate | 23°C | ASTMD3985 | 10 | cm³·mm/m²/atm/24hr |
| Water vapor permeability | 38°C,100%RH | ASTMF1249 | 7.0 | g/m²/24hr |
| Secant modulus | MD | ASTMD882 | 1900 | Mpa |
| TD | ASTMD882 | 1900 | Mpa | |
| elongation | MD:Yield | ASTMD882 | 4.0 | % |
| TD:Yield | ASTMD882 | 4.0 | % | |
| MD:Break | ASTMD882 | 400 | % | |
| TD:Break | ASTMD882 | 400 | % | |
| Elmondov tear strength | MD | ASTMD1922 | 1400 | g |
| TD | ASTMD1922 | 1700 | g | |
| Tensile strength | MD:Yield | ASTMD882 | 52.0 | Mpa |
| TD:Yield | ASTMD882 | 52.0 | Mpa | |
| MD:Break | ASTMD882 | 59.0 | Mpa | |
| TD:Break | ASTMD882 | 55.0 | Mpa | |
| Falling hammer impact 3 | -18°C | ASTMD1709A | 500 | g |
| 23°C | ASTMD1709A | 400 | g | |
| Tear resistance of pants 4 | TD | ISO6383-1 | 36.0 | N/mm |
| MD | ISO6383-1 | 36.0 | N/mm | |
| CarbonDioxidePermeability5 | 23°C | ASTMD1434 | 49 | cm³·mm/m²/atm/24hr |
| Resistance to tear propagation 6 | M.D.:23°C | ASTMD1938 | 36 | kN/m |
| T.D.:23°C | ASTMD1938 | 36 | kN/m |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | -40°C,2.50mm,EnergyatPeakLoad | ASTMD3763 | 41.0 | J |
| -40°C,3.20mm,EnergyatPeakLoad | ASTMD3763 | 50.0 | J | |
| 23°C,2.50mm,EnergyatPeakLoad | ASTMD3763 | 28.0 | J | |
| 23°C,3.20mm,EnergyatPeakLoad | ASTMD3763 | 33.0 | J | |
| -40°C,2.50mm,能量to力量峰值8,9 | ISO6603-2 | 35.0 | J | |
| -40°C,3.20mm,能量to力量峰值8,9 | ISO6603-2 | 36.0 | J | |
| 23°C,2.50mm,能量to力量峰值8,9 | ISO6603-2 | 40.0 | J | |
| 23°C,3.20mm,能量to力量峰值8,9 | ISO6603-2 | 44.0 | J | |
| Cantilever beam without notch impact strength | -40°C,3.20mm | ASTMD4812 | 无断裂 | |
| -30°C,3.20mm | ASTMD4812 | 无断裂 | ||
| -20°C,3.20mm | ASTMD4812 | 无断裂 | ||
| 23°C,3.20mm | ASTMD4812 | 无断裂 | ||
| -40°C7 | ISO180/1U | 无断裂 | ||
| -30°C7 | ISO180/1U | 无断裂 | ||
| -20°C7 | ISO180/1U | 无断裂 | ||
| 23°C7 | ISO180/1U | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale,23°C | ASTMD785 | 106 | |
| R-Sale,23°C | ISO2039-2 | 109 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | ASTMD1003 | 0.80 | % | |
| transmissivity | 常规 | ASTMD1003 | 89.0 | % |
| Total | ASTMD1003 | 91.0 | % | |
| gloss | 45° | ASTMD2457 | 108 | |
| transparency | ASTMD1746 | 85.0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.