PA9T POTICON NTB935C OTSUKAC JAPAN
98
- Unit Price:
- $7005 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow | 0.40 | % | |
| Across Flow | 1.6 | % | ||
| Moisture Absorption | Equilibrium | ASTM D570 | 0.18 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Break | ASTM D638 | 2.0 | % |
| Flexural Modulus | ASTM D790 | 11000 | Mpa | |
| Flexural Strength | ASTM D790 | 205 | Mpa | |
| Tensile Strength | ASTM D638 | 113 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Coefficient of Linear Thermal Expansion (Flow) | ASTM D696 | 1.5E-5 | cm/cm/°C | |
| Heat Distortion | ASTM D648 | 267 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Injection Pressure | 50.0 到 100 | Mpa | ||
| Processing (Melt) Temp | 310 到 330 | °C | ||
| Mold Temperature | 140 到 150 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | M-Scale | ASTM D785 | 99 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.