Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 24hr | ASTMD570 | 0.37 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tearing Strength | | Kg/m | 8.1 | |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD:3.18mm | ASTMD696 | 5.6E-05 | cm/cm/°C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.18mm | ASTMD648 | 207 | °C |
Glass Transition Temperature | | ASTME1356 | 220 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Constant | | ASTMD150 | 3.45 | |
Volume Resistivity | | ASTMD257 | 9E+15 | ohms·cm |
Dielectric Strength | 0.0250mm | ASTMD149 | 190 | KV/mm |
Film | Test Condition | Test Method | Test Result | Unit |
---|
Tearing Strength | | ASTMD1922 | 140 | gf |
面积系数 | | | 149 | ft²/lb/mil |
Film Thickness - Tested) | -- | | 25 | µm |
Film Thickness - Tested) | --2 | | 50 | µm |
Film Thickness - Tested) | --3 | | 130 | µm |
Secant Modulus | MD | ASTMD882 | 1590 | Mpa |
Secant Modulus | TD | ASTMD882 | 1980 | Mpa |
Tensile Elongation | MD:Yield | ASTMD882 | 9.2 | % |
Tensile Elongation | TD:Yield | ASTMD882 | 6.8 | % |
Tensile Elongation | MD:Break | ASTMD882 | 140 | % |
Tensile Elongation | TD:Break | ASTMD882 | 100 | % |
Tensile Strength | MD:Yield | ASTMD882 | 68.0 | Mpa |
Tensile Strength | TD:Yield | ASTMD882 | 59.0 | Mpa |
Tensile Strength | MD:Break | ASTMD882 | 92.0 | Mpa |
Tensile Strength | TD:Break | ASTMD882 | 70.0 | Mpa |
Gardner Impact | | ASTMD1709B | 750 | g |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | ASTMD2863 | 38 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.