Technical Data Sheet
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness (Shore A) | | ASTM D2240/ISO 868 | 86 | Shore A |
Shore Hardness (Shore D) | | ASTM D2240/ISO 868 | 33 | Shore D |
100% Secant | | ASTM D412/ISO 527 | 5 | Mpa/Psi |
300% Secant | | ASTM D412/ISO 527 | 9 | Mpa/Psi |
Tearing Strength | | ASTM D624/ISO 34 | 78 | n/mm² |
Flexural Strength | | ASTM D2630/ISO 4662 | 46 | % |
Abrasion | | ISO 4649 | 19 | mm³ |
Compression Set | | ISO 815 | 36 | % |
Compression Set | | ISO 815 | 11 | % |
Tensile Strain | Break, 23°C | DIN 53504 | 700 | % |
Tensile Storage Modulus | -20°C | ISO 6721 | 290 | Mpa |
Tensile Storage Modulus | 20°C | ISO 6721 | 31.0 | Mpa |
Tensile Storage Modulus | 60°C | ISO 6721 | 21.0 | Mpa |
Tensile Stress | Break, 23°C | DIN 53504 | 45.0 | Mpa |
Tensile Stress | 100% Strain, 23°C | DIN 53504 | 5.20 | Mpa |
Tensile Stress | 300% Strain, 23°C | DIN 53504 | 9.00 | Mpa |
Abrasion Resistance | | ISO 4649 | 30.0 | mm³ |
Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
---|
Rebound Resilience | | ISO 4662 | 44 | % |
Compression Set | 23°C, 72 hr | ISO 815 | 19 | % |
Compression Set | 70°C, 24 hr 3 | ISO 815 | 40 | % |
Compression Set | 70°C, 24 hr 5 | ISO 815 | 29 | % |
Processing | Test Condition | Test Method | Test Result | Unit |
---|
Melt Temperature | | | 200-220 | °C |
Mold Temperature | | | 20 | °C |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | < 80 | °C |
Processing (Melt) Temp | | | 220 到 240 | °C |
Mold Temperature | | | 20 | °C |
Extrusion | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | < 80 | °C |
Melt Temperature | | | 200 到 220 | °C |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore A, 1 sec, 23°C | ISO 7619 | 84 | |
Shore Hardness | Shore D, 1 sec, 23°C | ISO 7619 | 33 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.