Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 2781/JIS K7311 | 1.17 | |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 190°C/3.8kg | ASTMD1238 | 20to60 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Taber Abrasion Resistance | | ASTMD1044 | 40.0 | mg |
Abrasion-DIN | | DIN53516 | 20 | mm³ |
Shore Hardness (Shore A) | | ASTM D2240/ISO 868 | 64 | Shore A |
Tensile Strength | | ASTM D412/ISO 527 | 30 | Mpa/Psi |
Tearing Strength | | ASTM D624/ISO 34 | 30 | n/mm² |
Tearing Strength | | DIN 53515 | 30 | N/mm |
Abrasion | | ISO 4649 | 40 | mm³ |
Compression Set | | ISO 815 | 35 | % |
Compression Set | 70°C | DIN 53517 | 35 | % |
tensile strength | | DIN 53504-S2 | 30 | n/mm² |
tensile strength | 80℃水中21天 | DIN 53504-S2 | 25 | n/mm² |
Tensile Modulus | 100% | DIN 53504-S2 | 3 | n/mm² |
Tensile Modulus | 20% | DIN 53504-S2 | 1 | n/mm² |
Tensile Modulus | 300% | DIN 53504-S2 | 5 | n/mm² |
Elongation at break | 80℃水中21天 | DIN 53504-S2 | 900 | % |
Elongation at break | | DIN 53504-S2 | 750 | % |
Compression Set | | DIN 53517 | 20 | % |
Taber Abrasion Resistance | | DIN 53516 | 40 | mm³ |
Notched Izod Impact Strength | -30°C | DIN 53453 | 不破裂 | kJ/m² |
Notched Izod Impact Strength | +23°C | DIN 53453 | 不破裂 | kJ/m² |
Shore Hardness | | DIN 53505 | 64 | shoreA |
Tensile Modulus | Injection | ASTMD412 | 5.52 | Mpa |
Flexural Modulus | Injection | ASTMD790 | 8.96 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Glass Transition Temperature | | 内部方法 | -52.0 | °C |
SofteningPoint DMA | | 内部方法 | 109 | °C |
Vicat Softening Temperature | | ASTMD1525 | 66.0 | °C |
Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | 100%Strain | ASTMD412 | 3.65 | Mpa |
Tensile Stress | 300%Strain | ASTMD412 | 8.96 | Mpa |
Tensile Strength | | ASTMD412 | 23.4 | Mpa |
Tensile Elongation | Break | ASTMD412 | 760 | % |
Tearing Strength | | ASTMD624 | 64.8 | kN/m |
Compression Set | 23°C,22hr | ASTMD395B | 20 | % |
Compression Set | 70°C,22hr | ASTMD395B | 45 | % |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore A | ASTMD2240 | 61 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Density | | DIN 53479 | 1.17 | g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.