ASA GELOY™ CR7500 BK1041 SABIC INNOVATIVE US
76
- Unit Price:
- $2327 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 31MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Antistatic High mobility
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:Impact resistant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.80 | % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.50 | % |
| 平衡,23°C,50%RH | ISO62 | 0.20 | % | |
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 6.3 | g/10min |
| 260°C/5.0kg | ASTMD1238 | 11 | g/10min | |
| Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 6.60 | cm3/10min |
| 260°C/5.0kg | ISO1133 | 10.0 | cm3/10min | |
| Density | ISO1183 | 1.07 | g/cm³ | |
| ASTMD792 | 1.08 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | 屈服 | ASTMD638 | 40.0 | Mpa |
| 断裂 | ASTMD638 | 33.0 | Mpa | |
| Tensile Stress | 断裂 | ISO527-2/5 | 35.0 | Mpa |
| 屈服 | ISO527-2/5 | 43.0 | Mpa | |
| Tensile Strain | 断裂 | ISO527-2/5 | 19 | % |
| 屈服 | ISO527-2/5 | 3.3 | % | |
| Tensile Modulus | ASTMD638 | 1970 | Mpa | |
| ISO527-2/1 | 2040 | Mpa | ||
| Tensile Elongation | 屈服 | ASTMD638 | 3.6 | % |
| 断裂 | ASTMD638 | 60 | % | |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2170 | Mpa |
| ISO178 | 2060 | Mpa | ||
| Flexural Strength | ISO178 | 64.0 | Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 68.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa,未退火,3.20mm | ASTMD648 | 90.0 | °C |
| 1.8MPa,未退火,100mm跨距9 | ISO75-2/Ae | 88.0 | °C | |
| 1.8MPa,未退火,64.0mm跨距10 | ISO75-2/Af | 89.0 | °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 8.4E-05 | cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 8.4E-05 | cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 9.5E-05 | cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 9.5E-05 | cm/cm/°C | |
| Vicat Softening Temperature | ASTMD152511 | 98.0 | °C | |
| -- | ISO306/B50 | 102 | °C | |
| -- | ISO306/B120 | 105 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 30.0 | J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 14 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 60 | J/m |
| 23°C | ASTMD256 | 400 | J/m | |
| -30°C | ISO180/1A | 6.0 | kJ/m² | |
| 23°C | ISO180/1A | 15 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.