ASA GELOY™ XP4034 WH9B273 SABIC INNOVATIVE US
82
- Unit Price:
- $3681 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 31MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility High temperature resistan Antistatic Thermal stability Weather resistance
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| TD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Moisture Absorption | 24hr | ASTMD570 | 0.25 | % |
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 5.0 | g/10min |
| 260°C/5.0kg | ASTMD1238 | 14 | g/10min | |
| 280°C/3.8kg | ASTMD1238 | 24 | g/10min | |
| Density | ASTMD792 | 1.15 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | 屈服 | ASTMD638 | 62.1 | Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 57.0 | Mpa |
| 断裂 | ISO527-2/50 | 50.0 | Mpa | |
| Tensile Strain | 屈服 | ISO527-2/50 | 4.5 | % |
| 断裂 | ISO527-2/50 | 130 | % | |
| Tensile Modulus | ISO527-2/1 | 2500 | Mpa | |
| Tensile Elongation | 断裂 | ASTMD638 | 25 | % |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2520 | Mpa |
| ISO178 | 2500 | Mpa | ||
| Flexural Strength | ISO178 | 75.0 | Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 88.3 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa,未退火,6.40mm | ASTMD648 | 104 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 98.0 | °C | |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 116 | °C | |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 116 | °C | |
| Linear thermal expansion coefficient | MD：-20to150°C | ASTME831 | 7.2E-05 | cm/cm/°C |
| TD：-20to150°C | ASTME831 | 7.2E-05 | cm/cm/°C | |
| Vicat Softening Temperature | ISO306/B50 | 113 | °C | |
| Thermal Conductivity | ASTMC177 | 0.25 | W/m/K |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | -30°C,TotalEnergy | ASTMD3763 | 30.5 | J |
| 23°C,TotalEnergy | ASTMD3763 | 47.5 | J | |
| CharpyNotchedImpactStrength | 23°C | ISO179/1eA | 32 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 80 | J/m |
| 23°C | ASTMD256 | 320 | J/m | |
| -30°C | ISO180/1A | 7.0 | kJ/m² | |
| 23°C | ISO180/1A | 33 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.