MVLDPE DOWLEX™ 4404G STYRON US
168
- Unit Price:
- $2116 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 40.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:optical performance High toughness and optica Certified by Canadian HPF
- Application Areas:film Mainly used for packaging
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 4.0 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength(Break) | TD | ASTM D-882 | 32 | Mpa |
| MD | ASTM D-882 | 33 | Mpa | |
| Tensile Strength(Yield) | TD | ASTM D-882 | 5 | Mpa |
| MD | ASTM D-882 | 7 | Mpa | |
| Tensile Elongation?(Break) | TD | ASTM D-882 | 714 | % |
| MD | ASTM D-882 | 664 | % | |
| Tensile Modulus (2% Secant) | TD | ASTM D-882 | 63 | Mpa |
| Film Puncture Force | 陶氏企业测试 | 17 | J/cm³ | |
| Tensile Modulus (3% Secant) | MD | ASTM D-882 | 63 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature (DSC) | 内部方法 | 124 | °C | |
| Vicat Softening Temperature | ASTM D-1525 | 71 | °C | |
| Vicat Softening Temperature | ASTMD1525 | 71.1 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Carbon Dioxide Transmission Rate | 23°C,50.8µm | 内部方法 | 2000 | cm³·mm/m²/atm/24hr |
| Oxygen Transmission Rate | 23°C,51µm | ASTMD3985 | 450 | cm³·mm/m²/atm/24hr |
| Water Vapor Transmission Rate | 51µm | ASTMF1249 | 0.85 | g·mm/m²/atm/24hr |
| Secant Modulus | 2%Secant,MD:20μm | ASTMD882 | 58.8 | Mpa |
| 2%Secant,MD:51μm | ASTMD882 | 62.6 | Mpa | |
| 2%Secant,TD:20μm | ASTMD882 | 64.7 | Mpa | |
| 2%Secant,TD:51μm | ASTMD882 | 63.0 | Mpa | |
| Tensile Elongation | MD:Break,20μm | ASTMD882 | 500 | % |
| MD:Break,51μm | ASTMD882 | 660 | % | |
| TD:Break,20μm | ASTMD882 | 710 | % | |
| TD:Break,51μm | ASTMD882 | 710 | % | |
| Elmendorf Tear Strength | MD:20µm | ASTMD1922 | 330 | g |
| MD:51µm | ASTMD1922 | 960 | g | |
| TD:20µm | ASTMD1922 | 500 | g | |
| TD:51µm | ASTMD1922 | 1100 | g | |
| Tensile Strength | MD:Yield,20μm | ASTMD882 | 7.00 | Mpa |
| MD:Yield,51μm | ASTMD882 | 6.76 | Mpa | |
| TD:Yield,20μm | ASTMD882 | 4.92 | Mpa | |
| TD:Yield,51μm | ASTMD882 | 6.34 | Mpa | |
| MD:Break,20μm | ASTMD882 | 36.9 | Mpa | |
| MD:Break,51μm | ASTMD882 | 32.6 | Mpa | |
| TD:Break,20μm | ASTMD882 | 29.1 | Mpa | |
| TD:Break,51μm | ASTMD882 | 32.4 | Mpa | |
| Gardner Impact | 20µm | ASTMD1709B | >850 | g |
| 51µm | ASTMD1709B | >850 | g | |
| Film Puncture Force | 20µm | 内部方法 | 18.9 | J/cm³ |
| 51µm | 内部方法 | 17.5 | J/cm³ |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | ASTM D-1003 | 1.8 | % | |
| 20.3µm | ASTMD1003 | 0.60 | % | |
| 50.8µm | ASTMD1003 | 1.8 | % | |
| Gloss | 45° | ASTM D-2457 | 90 | |
| 45°,20.3µm | ASTMD2457 | 92 | ||
| 45°,50.8µm | ASTMD2457 | 90 | ||
| Transmittance | 20.3µm | ASTMD1746 | 99.0 | |
| 50.8µm | ASTMD1746 | 99.0 | ||
| ASTM D-1746 | 99 |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792 | 0.904 | g/cm³ | |
| Melt Mass-Flow Rate | ASTM D1238 | 4 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.