MVLDPE DOWLEX™ 2045G STYRON US

174

Unit Price:
$1466 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:high strength
Application Areas:film
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	℃/Kg	ASTMD1238	1.0	g/10min
Melt Mass-Flow Rate	Melt Mass-Flow Rate	厚度		50.8	microns

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation (Break MD)	50.8um	ASTM D-882	830	%
Tensile Elongation (Break TD)	50.8um	ASTM D-882	890	%
Secant Modulus (MD)	2% Secant，50.8um	ASTM D-882	194	Mpa
Secant Modulus (TD)	2% Secant，50.8um	ASTM D-882	233	Mpa
Tensile Strength (Break TD)	50.8um	ASTM D-882	55.1	Mpa
Tensile Strength (Break TD)	50.8um	ASTM D-882	49.8	Mpa
Tensile Strength		ASTMD882	10.89	Mpa
	Tensile Strength		ASTMD882	12.29	Mpa
		Tensile Strength		ASTMD882	55.11	Mpa
		Tensile Strength	Tensile Strength		ASTMD882	49.81	Mpa
Tensile Elongation	Break	ASTMD882	827	%
Tensile Elongation	Tensile Elongation	Break	ASTMD882	889	%
Tensile Strength (Yield TD)	50.8um	ASTM D-882	12.3	Mpa
Tensile Strength (Yield MD)	50.8um	ASTM D-882	10.9	Mpa
Elmendorf Tear Strength		ASTMD192	902	g
Elmendorf Tear Strength	Elmendorf Tear Strength		ASTMD192	1200	g
Secant Modulus		ASTMD882	194.4	Mpa
Secant Modulus	Secant Modulus		ASTMD882	232.6	Mpa
Gardner Impact		ASTMD1709	288	g
Tensile Strength			235	ft-lbf/in3

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ASTM1525	108	°C
Vicat Softening Temperature	Vicat Softening Temperature	Melting Temperature	陶氏化学方法(DSC	122	°C
Melting temperature		Internal Method	122	°C
Vicat Softening Temperature		ASTM D-1525	108	°C

Processing	Test Condition	Test Method	Test Result	Unit
Melt Temperature			232	°C

Other	Test Condition	Test Method	Test Result	Unit
Film Puncture Force	50.8um	Internal Method	19.4	J/cm³
Tearing Strength (MD)	50.8um	ASTM D-882	346	J/cm³
Tearing Strength (TD)	50.8um	ASTM D-882	351	J/cm4

optical performance	Test Condition	Test Method	Test Result	Unit
Gloss	45°，50.8um	ASTM D-2457	60
Gloss	Gloss		ASTM2457	60
Haze		ASTMD1003	10	%
Haze	50.8um	ASTM D-1003	10	%

Physical	Test Condition	Test Method	Test Result	Unit
Film Thickness			50.8	um
Melt Mass-Flow Rate	190℃/2.16kg	ASTM D-1238	1	g/10min
Density		ASTM D-792	0.92	g/m3

Other performance	Test Condition	Test Method	Test Result	Unit
Elmendorf Tear Strength		ASTMD1922	17.8	g/micron
Elmendorf Tear Strength	Elmendorf Tear Strength		ASTMD1922	23.6	g/micron
Tensile Strength		ASTMD882	4176	ft-lbf/in3
Tensile Strength	Tensile Strength		ASTMD882	4241	ft-lbf/in3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.