Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | ℃/Kg | ASTMD1238 | 1.0 | g/10min |
| Melt Mass-Flow Rate | 厚度 | | 50.8 | microns |
| Melt Mass-Flow Rate | Antiblock水平 | | 2500 | ppm |
| Melt Mass-Flow Rate | 滑水平 | | 1000 | ppm |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | | ASTMD882 | 8.267 | Mpa |
| Tensile Strength | | ASTMD882 | 8.811 | Mpa |
| Tensile Strength | | ASTMD882 | 38.04 | Mpa |
| Tensile Strength | | ASTMD882 | 36.54 | Mpa |
| Tensile Elongation | Break | ASTMD882 | 572 | % |
| Tensile Elongation | Break | ASTMD882 | 612 | % |
| Elmendorf Tear Strength | | ASTMD192 | 780 | g |
| Elmendorf Tear Strength | | ASTMD192 | 975 | g |
| Secant Modulus | | ASTMD882 | 180.9 | Mpa |
| Secant Modulus | | ASTMD882 | 204.4 | Mpa |
| Tensile Strength | | | 18 | ft-lbf/in3 |
| Gardner Impact | | ASTMD1709 | >=850 | g |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTM1525 | 100 | °C |
| Vicat Softening Temperature | Melting Temperature | 陶氏化学方法(DSC | 123 | °C |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Gloss | | ASTM2457 | 64 | |
| Haze | | ASTMD1003 | 13 | % |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Film Puncture Force | | | 5.76 | J |
| Peak Melting Temperature | | | 95.0 | °C |
| Elmendorf Tear Strength | | ASTMD1922 | 15.4 | g/micron |
| Elmendorf Tear Strength | | ASTMD1922 | 19.19 | g/micron |
| Tensile Strength | | ASTMD882 | 168 | ft-lbf/in3 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.