Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 1.0 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Gardner Impact | 20.3um | ASTM D-1709A | 130 | g |
| 50.8um | ASTM D-1709A | 280 | g | |
| Tensile Elongation (Break MD) | 20.3um | ASTM D-882 | 480 | % |
| 50.8um | ASTM D-882 | 670 | % | |
| Tensile Elongation (Break TD) | 20.3um | ASTM D-882 | 750 | % |
| 50.8um | ASTM D-882 | 770 | % | |
| Elmendorf Tear Strength (TD) | 20.3um | ASTM D-1922 | 580 | g |
| 50.8um | ASTM D-1922 | 1200 | g | |
| Elmendorf Tear Strength (MD) | 50.8um | ASTM D-1922 | 740 | g |
| 20.3um | ASTM D-1922 | 440 | g | |
| Secant Modulus (MD) | 2% Secant，50.8um | ASTM D-882 | 196 | Mpa |
| 20.3um | ASTM D-882 | 227 | Mpa | |
| Secant Modulus (TD) | 20.3um | ASTM D-882 | 247 | Mpa |
| 2% Secant，50.8um | ASTM D-882 | 234 | Mpa | |
| Tensile Strength (Break TD) | 20.3um | ASTM D-882 | 49.2 | Mpa |
| 50.8um | ASTM D-882 | 44.3 | Mpa | |
| Tensile Strength (Break TD) | 50.8um | ASTM D-882 | 51.9 | Mpa |
| 20.3um | ASTM D-882 | 60.4 | Mpa | |
| Tensile Strength (Yield TD) | 50.8um | ASTM D-882 | 12.6 | Mpa |
| 20.3um | ASTM D-882 | 13.1 | Mpa | |
| Tensile Strength (Yield MD) | 20.3um | ASTM D-882 | 12.7 | Mpa |
| 50.8um | ASTM D-882 | 11.8 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ASTM D-1525 | 104 | °C | |
| Melting temperature | Internal Method | 122 | °C | |
| Melting temperature (DSC) | 内部方法 | 122 | °C | |
| Vicat Softening Temperature | ASTMD1525 | 104 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film Thickness - Tested) | 内部方法 | 25 | µm | |
| Film Puncture Energy | 内部方法 | 1.24 | J | |
| Film Puncture Force | 内部方法 | 31.1 | N | |
| Tensile Modulus | MD | ASTMD882 | 110 | J/cm³ |
| TD | ASTMD882 | 114 | J/cm³ | |
| Secant Modulus | 1%Secant,MD | ASTMD882 | 211 | Mpa |
| 2%Secant,MD | ASTMD882 | 172 | Mpa | |
| 1%Secant,TD | ASTMD882 | 234 | Mpa | |
| 2%Secant,TD | ASTMD882 | 189 | Mpa | |
| Tensile Elongation | MD:Break | ASTMD882 | 540 | % |
| TD:Break | ASTMD882 | 660 | % | |
| Elmendorf Tear Strength | MD | ASTMD1922 | 440 | g |
| TD | ASTMD1922 | 630 | g | |
| Tensile Strength | MD:Yield | ASTMD882 | 13.4 | Mpa |
| TD:Yield | ASTMD882 | 14.1 | Mpa | |
| MD:Break | ASTMD882 | 46.1 | Mpa | |
| TD:Break | ASTMD882 | 35.3 | Mpa | |
| Gardner Impact | ASTMD1709A | 180 | g | |
| Film Puncture Force | 内部方法 | 6.21 | J/cm³ |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | 221-232 | °C |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tearing Strength (MD) | 20.3um | ASTM D-882 | 240 | J/cm4 |
| 50.8um | ASTM D-882 | 273 | J/cm5 | |
| Tearing Strength (TD) | 50.8um | ASTM D-882 | 292 | J/cm6 |
| 20.3um | ASTM D-882 | 304 | J/cm³ | |
| Film Puncture Force | 20.3um | Internal Method | 11.4 | J/cm³ |
| 50.8um | Internal Method | 9.76 | J/cm³ |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | 20.3um | ASTM D-1003 | 7 | % |
| 50.8um | ASTM D-1003 | 10 | % | |
| ASTMD1003 | 20 | % | ||
| Gloss | 45°，20.3um | ASTM D-2457 | 70 | |
| 45°，50.8um | ASTM D-2457 | 67 | ||
| 45° | ASTMD2457 | 34 |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D-792 | 0.922 | g/m3 | |
| Melt Mass-Flow Rate | 190℃/2.16kg | ASTM D-1238 | 1 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.