Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 230°C/2.16kg | ASTMD1238,ISO1133 | 2.0 | g/10min |
| Peak Crystallization Temperature | | 内部方法 | 35 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus(1% Secant) | Compression Molded | ASTMD790 | 359 | Mpa |
| Tensile Elongation | Break,Compression Molded | ASTMD638 | 680 | % |
| Tensile Strength | Break,Compression Molded | ASTMD638 | 26.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTMD1525 | 94.0 | °C |
| Melting temperature (DSC) | | 内部方法 | 107 | °C |
| Glass Transition Temperature | | 内部方法 | -17.0 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore A,Compression Molded | ASTMD2240 | 96 | |
| Shore Hardness | Shore D,Compression Molded | ASTMD2240 | 54 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Gardner | 20°,1000μm,Compression Molded | ASTMD523 | 108 | |
| Gardner | 60°,1000μm,Compression Molded | ASTMD523 | 119 | |
| Haze | 2000μm,Injection | ASTMD1003 | 18 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.