Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 3.0 | g/10min |
| Environmental Stress Cracking Resistance | | ASTMD1693B | >1000 | hr |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus | | ISO178 | 72.0 | Mpa |
| Tensile Stress | Break | ISO R527-1966 | 31.0 | Mpa |
| Tensile Strain | Break | ISO R527-1966 | 820 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ISO306/A | 80.0 | °C |
| Brittleness Temperature | | ASTMD746 | <-76.0 | °C |
| Melting temperature (DSC) | | ISO11357 | 96.0 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Secant Modulus (TD) | | ASTMD882 | 65.0 | Mpa |
| Gardner Impact | Blown Film | ASTMD1709 | >32 | g |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore D | ISO868 | 43 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Gloss | 45° | ASTMD2457 | 82 | |
| Haze | | ASTMD1003A | 2.0 | % |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| PunctureResistance | | 内部方法 | 26.5 | J/cm |
| SealingInitialTemperature | | ASTMF88 | 80 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.