COC TOPAS® 8007F-600 JAPAN POLYPLASTIC
100
- Unit Price:
- $12376 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 22.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Dimensional stability Chemical resistance
- Application Areas:LCD application Optical applications
- Color:--
- Grade:Food grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | (23°C,24hr) | ISO62 | 0.01 | % |
| Saturation,23°C | ISO62 | 0.010 | % | |
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 1.8 | g/10min |
| 230°C/2.16kg | ISO1133 | 10 | g/10min | |
| Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 2.00 | cm3/10min |
| 230°C/2.16kg | ISO1133 | 11.0 | cm3/10min | |
| Melt Mass-Flow Rate | 260℃/2.16Kg | ISO1133 | 32 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 20 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 2.6 | kJ/m² |
| Tensile Elongation?(Break) | 23°C | ISO527-2 | 4.5 | % |
| Tensile Modulus | 23°C | ISO527-2 | 2600 | Mpa |
| Tensile Strength | 23°C | ISO527-2 | 63 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPaUnannealed | ISO75-2/Bf | 75 | °C |
| Vicat Softening Temperature | ISO306/B50 | 80 | °C | |
| 玻璃转化温度 | ISO11357-2 | 78 | °C | |
| Glass Transition Temperature | ISO11357-2 | 78.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume Resistivity | IEC60093 | 1E+14 | Ω.cm | |
| Dielectric Constant | 23°C | IEC60250 | 2.35 | 1kHz |
| Dissipation Factor? | 相对漏电起痕指数 | IEC60112 | 600 | V |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film Thickness - Tested) | 70 | µm | ||
| Water Vapor Transmission Rate | 70µm,23°C,CastFilm,85%RH | ASTMF1249 | 0.10 | g·mm/m²/atm/24hr |
| Tensile Modulus | MD:70µm,铸造薄膜 | ISO527-3/1 | 2100 | Mpa |
| TD:70µm,铸造薄膜 | ISO527-3/1 | 1700 | Mpa | |
| Tensile Stress | MD:Break,70μm,铸造薄膜 | ISO527-3/50 | 55.0 | Mpa |
| TD:Break,70μm,铸造薄膜 | ISO527-3/50 | 50.0 | Mpa | |
| Tensile Elongation | MD:Break,70μm,铸造薄膜 | ISO527-3/50 | 3.4 | % |
| TD:Break,70μm,铸造薄膜 | ISO527-3/50 | 3.4 | % |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Light Transmittance (2000μm) | ISO13468-2 | 91 | % | |
| Haze | 70.0µm,铸造薄膜 | ISO14782 | >2.0 | % |
| Refractive index of light | ISO489 | 1.53 | °C | |
| Gloss | 60°,70.0µm,铸造薄膜 | ISO2813 | >100 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.