Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Across Flow | ISO 294-4 | 0.40 | % |
| Modeling Shrinkage | 流量 | ISO 294-4 | 0.20 | % |
| Melt Volume flow Rate | 275°C/2.16 kg | ISO 1133 | 8.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ISO 527-2 | -- | Mpa |
| Tensile Stress | Yield | ISO 527-2 | -- | Mpa |
| Tensile Strain | Yield | ISO 527-2 | -- | % |
| Nominal Tensile Strain at Break | | ISO 527-2 | > 50 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 85.0 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 73.0 | °C |
| Glass Transition Temperature | | ISO 11357-2 | 101 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Time | | | 4.0 到 6.0 | hr |
| Drying Temperature | | | 80 | °C |
| Processing (Melt) Temp | | | 260 到 300 | °C |
| Mold Temperature | | | 20 到 80 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | -- | |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | -- | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore D, 15 sec | ISO 7619-1 | 76 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Transmittance | | ISO 13468 | 92.0 | % |
| Transmittance | Renewable Carbon Conent | CSA LISTED | 64 到 66 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.