Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD：1.00mm2 | % | 0.30到0.70 | -- |
| Shrinkage rate | MD：3.00mm3 | % | 0.70到1.3 | -- |
| Water absorption rate | 23°C,24hr | % | 0.30 | -- |
| Water absorption rate | Saturation,23°C | % | 4.0 | -- |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | -40°C | MPa | 85.0 | -- |
| Tensile stress | 23°C | MPa | 55.0 | 40.0 |
| Tensile stress | 80°C | MPa | 25.0 | -- |
| Tensile strain | Break,23°C | % | 50 | |
| Bending modulus | -40°C | MPa | 2300 | -- |
| Bending modulus | 23°C | MPa | 2000 | 900 |
| Bending modulus | 80°C | MPa | 500 | -- |
| Bending stress | 23°C | MPa | 95.0 | 55.0 |
| Taber abraser | 1000Cycles | mg | 4.00 | -- |
| Compressive stress | 23°C | MPa | 65.0 | -- |
| shear strength | 23°C | MPa | 50.0 | 45.0 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 1.2E-04 | -- |
| Melting temperature | | °C | 225 | -- |
| specific heat | | J/kg/°C | 1900 | -- |
| thermal conductivity | | W/m/K | 0.25 | -- |
| Hot deformation temperature | 0.45MPa,Unannealed | °C | 180 | -- |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | ohms·cm | 1.0E+13到1.0E+14 | -- |
| Dissipation factor 4 | 23°C,50Hz | | 0.040 | -- |
| Dissipation factor 4 | 23°C,1kHz | | 0.040 | -- |
| Dissipation factor 4 | 23°C,1MHz | | 0.020 | -- |
| Dielectric constant 4 | 23°C,50Hz | | 3.90 | -- |
| Dielectric constant 4 | 23°C,1kHz | | 3.60 | -- |
| Dielectric constant 4 | 23°C,1MHz | | 3.10 | -- |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | 23°C | | 无断裂 | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R-Sale,23°C | | 116 | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.