Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:2.00mm | ISO294-4 | 0.50到0.70 | % |
Modeling Shrinkage | MD:2.00mm | ISO294-4 | 0.30到0.45 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.17 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break,23°C | ISO527-2/5 | 130 | Mpa |
Tensile Stress | Break,60°C | ISO527-2/5 | 125 | Mpa |
Tensile Stress | Break,90°C | ISO527-2/5 | 115 | Mpa |
Tensile Stress | Break,120°C | ISO527-2/5 | 100 | Mpa |
Tensile Stress | Break,150°C | ISO527-2/5 | 90.0 | Mpa |
Tensile Strain | Break,23°C | ISO527-2/5 | 2.0 | % |
Tensile Strain | Break,60°C | ISO527-2/5 | 2.1 | % |
Tensile Strain | Break,90°C | ISO527-2/5 | 2.3 | % |
Tensile Strain | Break,120°C | ISO527-2/5 | 2.4 | % |
Tensile Strain | Break,150°C | ISO527-2/5 | 2.5 | % |
Tensile Modulus | 23°C | ISO527-2/1 | 9600 | Mpa |
Tensile Modulus | 60°C | ISO527-2/1 | 9400 | Mpa |
Tensile Modulus | 90°C | ISO527-2/1 | 9200 | Mpa |
Tensile Modulus | 120°C | ISO527-2/1 | 9000 | Mpa |
Tensile Modulus | 150°C | ISO527-2/1 | 8600 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 215 | °C |
Deflection Temperature Under Load? | 连续使用温度3 | | 185 | °C |
Vicat Softening Temperature | | ISO306/B50 | 220 | °C |
Linear thermal expansion coefficient | MD:30to100°C | ISO11359-2 | 4E-06 | cm/cm/°C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 25 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | V-0 | |
UL flame retardant rating | 3.0mm | UL94 | V-0 | |
Oxygen Index | | ASTMD2863 | 40 | % |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
DimensionalStability | | | 74.0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.