Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD:24hr | ASTMD955 | 0.20到0.40 | % |
| Modeling Shrinkage | TD:24hr | ASTMD955 | 0.50到0.70 | % |
| Melt Mass-Flow Rate | 367°C/6.6kg | ASTMD1238 | 31 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| fracture | | ISO527-2/5 | 156 | Mpa |
| fracture | | ISO527-2/5 | 2.3 | % |
| Break | | ASTMD638 | 158 | Mpa |
| --6 | | ISO178 | 8410 | Mpa |
| Break,50.0mm Span | | ASTMD790 | 224 | Mpa |
| Break | | ASTMD638 | 2.4 | % |
| --2 | | ASTMD638 | 9170 | Mpa |
| 50.0mm Span | | ASTMD790 | 8140 | Mpa |
| --7 | | ISO178 | 225 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| 1.8MPa, Unannealed,6.40mm | | ASTMD648 | 197 | °C |
| 1.8MPa, Unannealed,64.0mm Span | | ISO75-2/Af | 201 | °C |
| Linear thermal expansion coefficient | MD:40to120°C | ASTME831 | 1.6E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD:40to120°C | ASTME831 | 6.3E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | ASTMD257 | 4E+05 | ohms |
| Volume Resistivity | | ASTMD257 | 5.1E+05 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 3.6 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.600mm,TestingbySABIC | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.