Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD1 | 内部方法 | 0.50到0.70 | % |
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.50到0.70 | % |
Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.50到0.70 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 1.8 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.60 | % |
Melt Mass-Flow Rate | 367°C/6.6kg | ASTMD1238 | 16 | g/10min |
Melt Volume flow Rate | 360°C/5.0kg | ISO1133 | 8.50 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
--9 | | ISO178 | 123 | Mpa |
--8 | | ISO178 | 3080 | Mpa |
yield | | ISO527-2/5 | 95.0 | Mpa |
yield | | ISO527-2/5 | 8.5 | % |
fracture | | ISO527-2/5 | 78.0 | Mpa |
fracture | | ISO527-2/5 | 17 | % |
--2 | | ASTMD638 | 3520 | Mpa |
Yield | | ASTMD638 | 96.5 | Mpa |
Break | | ASTMD638 | 50 | % |
50.0mm Span | | ASTMD790 | 3170 | Mpa |
Break | | ASTMD638 | 96.5 | Mpa |
Yield | | ASTMD638 | 6.0 | % |
Break,50.0mm Span | | ASTMD790 | 159 | Mpa |
Yield,100mm Span | | ASTMD790 | 155 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
1.8MPa, Unannealed,3.20mm | | ASTMD648 | 217 | °C |
Flow:-40 to 150°C | | ASTME831 | 5E-05 | cm/cm/°C |
Flow:23 to 150°C | | ISO11359-2 | 5E-05 | cm/cm/°C |
Flow:-40 to 150°C | | ASTME831 | 5E-05 | cm/cm/°C |
Flow:23 to 150°C | | ISO11359-2 | 5E-05 | cm/cm/°C |
1.8MPa, Unannealed,64.0mm Span | | ISO75-2/Af | 228 | °C |
Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
1.8MPa, Unannealed,6.40mm | | ASTMD648 | 230 | °C |
0.45MPa, Unannealed,6.40mm | | ASTMD648 | 237 | °C |
Thermal Conductivity | | ASTME1530 | 0.22 | W/m/K |
-- | | ASTMD1525,ISO306/B501217 | 242 | °C |
-- | | ISO306/B120 | 238 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Comparative Tracking Index | | IEC60112 | 175 | V |
Dielectric Constant | 100Hz | ASTMD150 | 3.41 | |
Dielectric Constant | 1kHz | ASTMD150 | 3.41 | |
Dissipation Factor? | 50Hz | IEC60250 | 0.025 | |
Dissipation Factor? | 60Hz | IEC60250 | 0.025 | |
Dissipation Factor? | 100Hz | IEC60250 | 8E-03 | |
Dissipation Factor? | 1kHz | IEC60250 | 1E-03 | |
Dissipation Factor? | 1MHz | IEC60250 | 7E-03 | |
Dielectric Strength | 3.20mm,inOil | ASTMD149 | 17 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 33.9 | J |
23°C | | ASTMD256 | 69 | J/m |
23°C | | ASTMD4812,ISO180/1U | 无断裂 | |
-30°C | | ASTMD256 | 74 | J/m |
-30°C15 | | ISO180/1U | 无断裂 | |
-30°C13 | | ISO180/1A | 5.4 | kJ/m² |
23°C14 | | ISO180/1A | 4.6 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 | |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 无断裂 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | H358/30 | ISO2039-1 | 141 | Mpa |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Haze | 2540µm | ASTMD1003 | 2.0 | % |
Transmittance | 2540µm | ASTMD1003 | 58.0 | % |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Glow Wire Flammability Index | 3.20mm | IEC60695-2-12 | 960 | °C |
Oxygen Index | | ISO4589-2 | 45 | % |
Glow Wire Ignition Temperature | 3.00mm | IEC60695-2-13 | 850 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.