Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | 23℃Saturation | ISO 62 | 1.25 | % |
| 23°C50RH | ISO 62 | 0.7 | % | |
| Modeling Shrinkage (Flow) | 内部测试方法 | 0.5-0.7 | % | |
| Melt Mass-Flow Rate | 360℃ 5kg | ISO 1133 | 25 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 23℃ 4.0mm A型Notched | ISO 180 | 4 | kJ/m² |
| Tensile Modulus | 1 Omm/min | ISO 527 | 3200 | Mpa |
| Tensile Strength | Yield50mm/min | ISO 527 | 105 | Mpa |
| Tensile Elongation | Yield50mm/min | ISO 527 | 6 | % |
| Flexural Modulus | 2.Omm/min | ISO 178 | 3200 | Mpa |
| Flexural Strength | Yield2.0mm/min | ISO 178 | 140 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa 4.0mm | ISO 75 | 195 | °C |
| Vicat Softening Temperature | 50℃/hr 10N | ISO 306 | 210 | °C |
| Coefficient of Linear Thermal Expansion | Flow23~150℃ | ISO 11359 | 0.000050 | cm/cm/℃ |
| Coefficient of Linear Thermal Expansion | 垂直23~150℃ | ISO 11359 | 0.000050 | cm/cm/℃ |
| Ball Indentation Hardness | ISO 11359-2 | 125 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.