PEI ULTEM™ 9085-1100 SABIC INNOVATIVE US
74
- Unit Price:
- $26976 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Low toxicity Low smoke
- Application Areas:Aircraft interior parts national defense Railway Applications Profile
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 295°C/6.6kg | ASTMD1238 | 8.9 | g/10min |
| Melt Volume flow Rate | 360°C/5.0kg | ISO1133 | 65.5 | cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.39 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.17 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Yield | ISO527-2/5 | 88.0 | Mpa |
| Break | ISO527-2/5 | 71.0 | Mpa | |
| Tensile Strain | Yield | ISO527-2/5 | 6.7 | % |
| Break | ISO527-2/5 | 50 | % | |
| Tensile Modulus | ISO527-2/1 | 3050 | Mpa | |
| Flexural Modulus | ISO178 | 2750 | Mpa | |
| Flexural Strength | ISO178 | 90.0 | Mpa | |
| Tensile Elongation | Yield | ASTMD638 | 7.0 | % |
| Tensile Modulus | ASTMD638 | 3440 | Mpa | |
| Tensile Strength | Yield | ASTMD638 | 84.0 | Mpa |
| Break | ASTMD638 | 74.0 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2920 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 138 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 72 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 153 | °C |
| Vicat Softening Temperature | ISO306/B120 | 173 | °C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 152 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 13 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FAAFlammability9 | FAR25.853 | <5 | ||
| OSU峰值放热速率10 | FAR25.853 | 36.0 | kW/m² | |
| OSU总放热量11 | FAR25.853 | 16.0 | kW·min/m² | |
| VerticalBurnTest-Testa | 60s),passesat | FAR25.853 | 2.0 | sec |
| Oxygen Index | ASTMD2863 | 49 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.