PEI ULTEM™ 1010FC-7101 SABIC INNOVATIVE US

Unit Price:
$22476 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Saturation, 23°C	ISO 62	1.3	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.70	%
Melt Volume flow Rate	340°C/5.0 kg	ISO 1133	13.0	cm3/10min
Modeling Shrinkage - Flow		内部方法	0.50 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress		ISO 178	160	Mpa
Flexural Modulus		ISO 178	3300	Mpa
Tensile Stress	Yield	ISO 527-2/50	105	Mpa
Tensile Stress	Tensile Stress	Break	ISO 527-2/50	85.0	Mpa
Tensile Strain	Yield	ISO 527-2/50	6.0	%
Tensile Strain	Tensile Strain	Break	ISO 527-2/50	60	%
Tensile Modulus		ISO 527-2/1	3200	Mpa
Taber Abrasion Resistance	1000 Cycles, 1000 g, CS-17 Wheel	内部方法	10.0	mg

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ISO 306/A50	215	°C
	Vicat Softening Temperature	--	ISO 306/B50	211	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	212	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过
Thermal Conductivity		ISO 8302	0.21	W/m/K
RTI		UL 746	170	°C
RTI Imp		UL 746	170	°C
RTI Elec		UL 746	170	°C
Linear thermal expansion coefficient	Flow : 23 to 150°C	ISO 11359-2	5.0E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 150°C	ISO 11359-2	5.0E-5	cm/cm/°C
Heat Deflection Temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	195	°C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	190	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	1.60 mm, in Oil	IEC 60243-1	28	KV/mm
Surface Resistivity		IEC 60093	> 1.0E+15	ohms
Volume Resistivity		IEC 60093	1.0E+15	ohms·cm
Relative Permittivity	50 Hz	IEC 60250	2.90
	Relative Permittivity	60 Hz	IEC 60250	2.90
	Relative Permittivity	Relative Permittivity	1 MHz	IEC 60250	2.90
Comparative Tracking Index	--	IEC 60112	150	V
Comparative Tracking Index	Comparative Tracking Index	Solution B	IEC 60112	100	V
Dissipation Factor?	50 Hz	IEC 60250	5.0E-4
	Dissipation Factor?	60 Hz	IEC 60250	5.0E-4
		Dissipation Factor?	1 MHz	IEC 60250	6.0E-3
		Dissipation Factor?	Dissipation Factor?	2.45 GHz	IEC 60250	2.5E-3

Injection	Test Result	Unit
Drying Temperature	150	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	370 到 410	°C
Mold Temperature	140 到 180	°C
Drying Time	4.0 到 6.0	hr
Rear Temperature	350 到 400	°C
Middle Temperature	360 到 410	°C
Front Temperature	370 到 420	°C
Nozzle Temperature	360 到 410	°C
Hopper Temperature	80 到 120	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod Impact Strength	-30°C	ISO 180/1A	5.0	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO 180/1A	5.0	kJ/m²
Unnotched Izod Impact Strength	-30°C	ISO 180/1U	无断裂
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ISO 180/1U	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness	H 358/30	ISO 2039-1	140	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	3.2 mm	IEC 60695-2-12	960	°C
Oxygen Index		ISO 4589-2	47	%
Flame Rating	0.75 mm	UL 94	V-0
Flame Rating	Flame Rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.