Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD1 | 内部方法 | 0.40到0.60 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 1.0 | % |
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.60 | % |
| Melt Volume flow Rate | 360°C/5.0kg | ISO1133 | 9.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Stress | | ISO178 | 185 | Mpa |
| Tensile Stress | Break | ISO527-2/5 | 115 | Mpa |
| Tensile Strain | Break | ISO527-2/5 | 4.0 | % |
| Flexural Modulus | | ISO178 | 4500 | Mpa |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 15.0 | mg |
| Tensile Modulus | | ISO527-2/1 | 4500 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| -- | | ISO306/A50 | 223 | °C |
| -- | | ISO306/B50 | 212 | °C |
| -- | | ISO306/B120 | 217 | °C |
| 0.45MPa, Unannealed,100mm Span | | ISO75-2/Be | 210 | °C |
| 1.8MPa, Unannealed,100mm Span | | ISO75-2/Ae | 205 | °C |
| Linear thermal expansion coefficient | MD:23to150°C | ISO11359-2 | 2.6E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD:23to150°C | ISO11359-2 | 6E-05 | cm/cm/°C |
| Thermal Conductivity | | ISO8302 | 0.24 | W/m/K |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | 30 | kJ/m² |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 30 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 140 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Index | | ISO4589-2 | 46 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.