Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:24hr | ASTMD955 | 0.010to0.050 | % |
Modeling Shrinkage | TD:24hr | ASTMD955 | 0.10to0.50 | % |
Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.11 | % |
Melt Mass-Flow Rate | 380°C/6.7kg | ASTMD1238 | 15 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Compressive Strength | | 内部方法 | 222 | Mpa |
Shearing Strength | | ASTMC273 | 120 | Mpa |
Shearing Strength | | ASTMC273 | 4660 | Mpa |
Poisson Ratio | | ASTMD638 | 0.40 | |
Tensile Modulus | | ASTMD638 | 38600 | Mpa |
Tensile Strength | Break | ASTMD638 | 272 | Mpa |
Flexural Modulus | 50.0mmSpan | ASTMD790 | 32600 | Mpa |
Tensile Stress | Break | ISO527-2/5 | 247 | Mpa |
Tensile Strain | Break | ISO527-2/5 | 0.90 | % |
Tensile Modulus | | ISO527-2/1 | 35500 | Mpa |
Tensile Elongation | Break | ASTMD638 | 1.0 | % |
Flexural Modulus | | ISO178 | 30600 | Mpa |
Flexural Strength | | ISO178 | 364 | Mpa |
Flexural Strength | Break,50.0mmSpan | ASTMD790 | 372 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 193 | °C |
Linear thermal expansion coefficient | MD:-40to150°C | ASTME831 | 2.7E-06 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-40to150°C | ASTME831 | 3.6E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | ASTMD257 | 4.1E+03 | ohms |
Volume Resistivity | | ASTMD257 | 4.5E+02 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 7.30 | J |
Notched Izod Impact Strength | 23°C | ISO180/1A | 6.9 | kJ/m² |
UnnotchedIzodImpactStrength7 | 23°C | ISO180/1U | 34 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Scale | ASTMD785 | 112 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.