PEI ULTEM™ HU2200-1H1000 SABIC INNOVATIVE US
82
- Unit Price:
- $8596 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Food contact Filler: Glass fiber reinf 20% Filler by weight
- Application Areas:packing auto parts medicine Medical/nursing supplies
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.30to0.50 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 1.0 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.55 | % | |
| Melt Mass-Flow Rate | 337°C/6.6kg | ASTMD1238 | 6.0 | g/10min |
| Melt Volume flow Rate | 360°C/5.0kg | ISO1133 | 7.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Yield | ASTMD638 | 4.0 | % |
| Tensile Modulus | ASTMD638 | 6890 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 131 | Mpa |
| Yield | ASTMD638 | 131 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 6850 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 225 | Mpa |
| Tensile Stress | Yield | ISO527-2/5 | 131 | Mpa |
| Break | ISO527-2/5 | 131 | Mpa | |
| Tensile Strain | Yield | ISO527-2/5 | 4.0 | % |
| Break | ISO527-2/5 | 4.0 | % | |
| Tensile Modulus | ISO527-2/1 | 6890 | Mpa | |
| Flexural Strength | ISO178 | 228 | Mpa | |
| Tensile Elongation | Break | ASTMD638 | 4.0 | % |
| Flexural Modulus | ISO178 | 6890 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 205 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 208 | °C |
| Vicat Softening Temperature | ASTMD152510 | 220 | °C | |
| -- | ISO306/B50 | 212 | °C | |
| -- | ISO306/B120 | 218 | °C | |
| Linear thermal expansion coefficient | MD：-20to150°C | ASTME831 | 2.5E-05 | cm/cm/°C |
| MD：23to150°C | ISO11359-2 | 2.5E-05 | cm/cm/°C | |
| TD：-40to150°C | ASTME831 | 5E-05 | cm/cm/°C | |
| TD：23to150°C | ISO11359-2 | 5E-05 | cm/cm/°C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 8.00 | J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 65 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 70 | kJ/m² |
| 23°C | ISO180/1A | 64 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.