PEI ULTEM™ HU1000 2H4D342 SABIC INNOVATIVE US
118
- Unit Price:
- $11084 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Middle flow Biocompatibility Steam sterilization
- Application Areas:Medical and nursing suppl Medical devices
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Moisture Absorption | 24hr | ASTMD570 | 0.25 | % |
| Saturation,23°C | ISO62 | 1.3 | % | |
| Equilibrium,23°C | ASTMD570 | 1.3 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.70 | % | |
| Melt Mass-Flow Rate | 337°C/6.6kg | ASTMD1238 | 9.0 | g/10min |
| Melt Volume flow Rate | 220°C/5.0kg | ISO1133 | 13.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | ISO178 | 3300 | Mpa | |
| Tensile Elongation | Yield | ASTMD638 | 7.0 | % |
| Tensile Modulus | ASTMD638 | 3580 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 90.0 | Mpa |
| Yield | ASTMD638 | 110 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 3440 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 173 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 60 | % |
| Tensile Stress | Yield | ISO527-2/5 | 105 | Mpa |
| Break | ISO527-2/5 | 85.0 | Mpa | |
| Tensile Strain | Yield | ISO527-2/5 | 6.0 | % |
| Break | ISO527-2/5 | 60 | % | |
| Tensile Modulus | ISO527-2/1 | 3200 | Mpa | |
| Flexural Strength | ISO178 | 160 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 201 | °C |
| Linear thermal expansion coefficient | MD：-20to150°C | ASTME831 | 5.6E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 5E-05 | cm/cm/°C | |
| TD：-20to150°C | ASTME831 | 5.4E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 5E-05 | cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 215 | °C |
| Vicat Softening Temperature | ASTMD152510 | 219 | °C | |
| -- | ISO306/B50 | 215 | °C | |
| -- | ISO306/B120 | 211 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative Tracking Index | CTI | UL746 | PLC4 | |
| High Amp Arc Ignition | HAI | UL746 | PLC3 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC2 | |
| Hot-wire Ignition | HWI | UL746 | PLC1 | |
| Dielectric Strength | 1.60mm,inAir | ASTMD149 | 33 | KV/mm |
| 1.60mm,in Oil | ASTMD149 | 28 | KV/mm | |
| Dielectric Constant | 1kHz | ASTMD150 | 3.15 | |
| Volume Resistivity | ASTMD257 | 1E+17 | ohms·cm | |
| Dissipation Factor? | 1kHz | ASTMD150 | 1.3E-03 | |
| 2.45GHz | ASTMD150 | 2.5E-03 | ||
| Arc Resistance | ASTMD495 | PLC5 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 4.0 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 6.0 | kJ/m² |
| 23°C | ISO180/1A | 6.0 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| NBSSmokeDensity-Flaming,Ds,4min | ASTME662 | 0.700 | ||
| Oxygen Index | ASTMD2863 | 47 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.