PEI ULTEM™ 1010 GY2E570 SABIC INNOVATIVE US

Unit Price:
$24666 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan transparent enhance Flame retardant
Application Areas:Food service sector
Color:--
Grade:Food grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24 hr	ASTM D570	0.25	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C	ASTM D570	1.3	%
Melt Mass-Flow Rate	337°C/6.6 kg	ASTM D1238	18	g/10 min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus		ASTM D638	3580	Mpa
Tensile Elongation	Yield	ASTM D638	7.0	%
Tensile Elongation	Tensile Elongation	Break	ASTM D638	60	%
Flexural Modulus	100 mm Span	ASTM D790	3510	Mpa
Flexural Strength	Yield, 100 mm Span	ASTM D790	165	Mpa
Taber Abrasion Resistance	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg
Tensile Strength	Yield	ASTM D638	110	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ASTM D15255	218	°C
Thermal Conductivity		ASTM C177	0.22	W/m/K
RTI		UL 746	170	°C
RTI Imp		UL 746	170	°C
RTI Elec		UL 746	170	°C
Coefficient of Linear Thermal Expansion (Flow)	-20 to 150°C	ASTM E831	5.6E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	207	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	198	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		UL 746	PLC 4
High Amp Arc Ignition		UL 746	PLC 3
Hot-wire Ignition		UL 746	PLC 1
Dielectric Constant	1 kHz	ASTM D150	3.15
Volume Resistivity		ASTM D257	1.0E+17	ohms·cm
Dissipation Factor?	1 kHz	ASTM D150	1.3E-3
Dissipation Factor?	Dissipation Factor?	2.45 GHz	ASTM D150	2.5E-3
Dielectric Strength	1.60 mm, in Air	ASTM D149	33	KV/mm
Dielectric Strength	Dielectric Strength	1.60 mm, in Oil	ASTM D149	28	KV/mm
High Voltage Arc Tracking Rate		UL 746	PLC 2
Arc Resistance		ASTM D495	PLC 5

Injection	Test Result	Unit
Drying Temperature	150	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	350 到 400	°C
Mold Temperature	135 到 165	°C
Drying Time	4.0 到 6.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	330 到 400	°C
Middle Temperature	340 到 400	°C
Front Temperature	345 到 400	°C
Nozzle Temperature	345 到 400	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Reverse Notch Izod Impact	3.20 mm	ASTM D256	1200	J/m
Gardner Impact	23°C	ASTM D3029	33.0	J
Unnotched Izod Impact Strength	23°C	ASTM D4812	1300	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTM D785	109

Flammability	Test Condition	Test Method	Test Result	Unit
Oxygen Index		ASTM D2863	44	%
Flame Rating	0.75 mm	UL 94	V-0
Flame Rating	Flame Rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.