Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 380°C/6.7kg | ASTMD1238 | 22 | g/10min |
Modeling Shrinkage | MD:24hr | ASTMD955 | 0.030to0.10 | % |
Modeling Shrinkage | TD:24hr | ASTMD955 | 0.10to0.60 | % |
Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.11 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2/5 | 248 | Mpa |
Tensile Strain | Break | ISO527-2/5 | 1.2 | % |
Tensile Elongation | Break | ASTMD638 | 1.3to1.4 | % |
Flexural Modulus | | ISO178 | 23100 | Mpa |
Flexural Strength | Break,50.0mmSpan | ASTMD790 | 341 | Mpa |
Flexural Strain (Break) | | ISO178 | 330 | % |
Compressive Strength | | 内部方法 | 244 | Mpa |
Shearing Strength | | ASTMC273 | 128 | Mpa |
Shearing Strength | | ASTMC273 | 4730 | Mpa |
Poisson Ratio | | ASTMD638 | 0.44 | |
Tensile Modulus | | ASTMD638 | 29500 | Mpa |
Tensile Strength | Break | ASTMD638 | 272 | Mpa |
Flexural Modulus | 50.0mmSpan | ASTMD790 | 23800 | Mpa |
Tensile Modulus | | ISO527-2/1 | 27600 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 195 | °C |
Linear thermal expansion coefficient | MD:-40to150°C | ASTME831 | 7.2E-06 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-40to150°C | ASTME831 | 5.8E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | ASTMD257 | 1E+03 | ohms |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 12.3 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.