Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | 内部方法 | 0.40 | % |
Modeling Shrinkage | TD | 内部方法 | 0.52 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
fracture | | ISO527-2/5 | 156 | Mpa |
fracture | | ISO527-2/5 | 1.2 | % |
Coefficient of Friction | Itself - Dynamic | ASTMD3702Modified | 0.52 | |
Break | | ASTMD638 | 3.0 | % |
50.0mm Span | | ASTMD790 | 6420 | Mpa |
--5 | | ISO178 | 7220 | Mpa |
--1 | | ASTMD638 | 8630 | Mpa |
Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 202 | Mpa |
Flexural Strength | Break,50.0mmSpan | ASTMD790 | 201 | Mpa |
Specific Wear Rate | | ASTMD3702Modified | 15.6 | 10^-10in^5-min/ft-lb-hr |
Break | | ASTMD638 | 157 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD:-40to40°C | ASTME831 | 1.4E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-40to40°C | ASTME831 | 5.1E-05 | cm/cm/°C |
1.8MPa, Unannealed,3.20mm | | ASTMD648 | 204 | °C |
1.8MPa, Unannealed,64.0mm Span | | ISO75-2/Af | 207 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 100kHz | ASTMD150 | 3.1E-03 | |
Surface Resistivity | | ASTMD257 | 2E+13 | ohms |
Dielectric Constant | 100kHz | ASTMD150 | 3.30 | |
Volume Resistivity | | ASTMD257 | 7.6E+16 | ohms·cm |
Dielectric Strength | 1.60mm,inOil | ASTMD149 | 31 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
23°C | | ASTMD4812 | 330 | J/m |
23°C | | ASTMD256 | 67 | J/m |
23°C7 | | ISO180/1A | 7.8 | kJ/m² |
23°C8 | | ISO180/1U | 26 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.