Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan transparent enhance Flame retardant
Application Areas:Food service sector
Color:--
Grade:Injection grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	24 hr	ASTM D570	0.25	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C	ASTM D570	1.3	%
Melt flow rate	337°C/6.6 kg	ASTM D1238	18	g/10 min
Shrinkage rate - flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus 2		ASTM D638	3580	Mpa
Elongation rate 3	Yield	ASTM D638	7.0	%
Elongation rate 3	Elongation rate 3	Break	ASTM D638	60	%
Bending modulus	100 mm Span	ASTM D790	3510	Mpa
bending strength	Yield, 100 mm Span	ASTM D790	165	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg
Tensile strength	Yield	ASTM D638	110	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature		ASTM D15255	218	°C
thermal conductivity		ASTM C177	0.22	W/m/K
RTI		UL 746	170	°C
RTI Imp		UL 746	170	°C
RTI Elec		UL 746	170	°C
Linear coefficient of thermal expansion - flow	-20 to 150°C	ASTM E831	5.6E-5	cm/cm/°C
Thermal deformation temperature under load	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	207	°C
Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	198	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 4
High arc combustion index (HAI) 7		UL 746	PLC 3
Hot wire ignition (HWI)		UL 746	PLC 1
Dielectric constant	1 kHz	ASTM D150	3.15
Volume resistivity		ASTM D257	1.0E+17	ohms·cm
Dissipation factor	1 kHz	ASTM D150	1.3E-3
Dissipation factor	Dissipation factor	2.45 GHz	ASTM D150	2.5E-3
Dielectric strength	1.60 mm, in Air	ASTM D149	33	KV/mm
Dielectric strength	Dielectric strength	1.60 mm, in Oil	ASTM D149	28	KV/mm
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 2
Arc resistance 6		ASTM D495	PLC 5

injection	Test Result	Unit
drying temperature	150	°C
Suggested maximum moisture content	0.020	%
Processing (melt) temperature	350 到 400	°C
Mold temperature	135 到 165	°C
drying time	4.0 到 6.0	hr
Suggested injection volume	40 到 60	%
Temperature at the rear of the barrel	330 到 400	°C
Temperature in the middle of the barrel	340 到 400	°C
Temperature at the front of the material cylinder	345 到 400	°C
Spray nozzle temperature	345 到 400	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	40 到 70	rpm
Exhaust hole depth	0.025 到 0.076	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Reverse notch impact	3.20 mm	ASTM D256	1500	J/m
Falling hammer impact	23°C	ASTM D3029	33.0	J
Non notched cantilever beam impact	23°C	ASTM D4812	1300	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ASTM D785	109

flammability	Test Condition	Test Method	Test Result	Unit
Extreme Oxygen Index		ASTM D2863	44	%
UL flame retardant rating	0.75 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.