Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.50to0.70 | % |
Moisture Absorption | 24hr | ASTMD570 | 0.22 | % |
Melt Mass-Flow Rate | 367°C/6.6kg | ASTMD1238 | 15 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Taber Abrasion Resistance | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 11.0 | mg |
Flexural Modulus | 100mmSpan | ASTMD790 | 4410 | Mpa |
Tensile Strength | Yield | ASTMD638 | 96.5 | Mpa |
Tensile Strength | Break | ASTMD638 | 92.4 | Mpa |
Tensile Elongation | Break | ASTMD638 | 10 | % |
Flexural Strength | Yield,100mmSpan | ASTMD790 | 145 | Mpa |
Flexural Strength | Break,100mmSpan | ASTMD790 | 145 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ASTMD15254 | 237 | °C |
RTIElec | | UL746 | 105 | °C |
Evolution Calendar intelligent importer | | UL746 | 105 | °C |
RTIStr | | UL746 | 105 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 214 | °C |
Linear thermal expansion coefficient | MD:-20to150°C | ASTME831 | 4.5E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-20to150°C | ASTME831 | 4.9E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | 1.60mm,inOil | ASTMD149 | 21 | KV/mm |
Dielectric Constant | 1kHz | ASTMD150 | 3.10 | |
Volume Resistivity | | ASTMD257 | 1E+17 | ohms·cm |
Dissipation Factor? | 1kHz | ASTMD150 | 1E-03 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Scale | ASTMD785 | 110 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | V-0 | |
Oxygen Index | | ASTMD2863 | 48 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.