PEI ULTEM™ ATX100 BK1343M SABIC INNOVATIVE US
39
- Unit Price:
- $7011 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength(Yield) | Compression Molded | MPa | ASTM D-638 | |
| Tensile Elongation?(Break) | Compression Molded | % | ASTM D-638 | |
| Tensile Strength(Break) | Compression Molded | MPa | ASTM D-638 | 18 |
| Gardner Impact | 50um，Blown Film | g | ASTM D-1709A | 210 |
| Coefficient of Friction | vs. Itself-Dynamic，Blown Film | ASTM D-1894 | ||
| Tensile Elongation (Break MD) | 50um，Blown Film | % | ASTM D-882 | 280 |
| Tensile Elongation (Break TD) | 50um，Blown Film | % | ASTM D-882 | |
| Elmendorf Tear Strength (TD) | 50um，Blown Film | g | ASTM D-1922 | 280 |
| Elmendorf Tear Strength (MD) | 50um，Blown Film | g | ASTM D-1922 | 340 |
| Tensile Strength (Break TD) | 50um，Blown Film | MPa | ASTM D-882 | 26 |
| Tensile Strength (Break TD) | 50um，Blown Film | MPa | ASTM D-882 | 28 |
| Secant modulus- | 50um，Blown Film | MPa | ASTM D-882 | |
| 50um，Blown Film | MPa | ASTM D-882 | 130 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ℃ | ASTM D-1525 |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 适配器温度 | ℃ | 210-225 |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | g/cm³ | ASTM D-1505 | 0.922 | |
| Melt Mass-Flow Rate | 190℃/2.16kg | g/10min | ASTM D-1238 | 0.12 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.