PEI ULTEM™ HU1010 7H1D395 SABIC INNOVATIVE NANSHA
116
- Unit Price:
- $19576 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Middle flow Biocompatibility Steam sterilization
- Application Areas:Medical and nursing suppl Medical devices
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 1.3 | % |
| Equilibrium,23°C | ASTMD570 | 1.3 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.70 | % | |
| Melt mass flow rate | 337°C/6.6kg | ASTMD1238 | 18 | g/10min |
| Melt volume flow rate | 360°C/5.0kg | ISO1133 | 25.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation rate 3 | Yield | ASTMD638 | 7.0 | % |
| Tensile modulus 2 | ASTMD638 | 3580 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 110 | Mpa |
| Break | ASTMD638 | 105 | Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 10.0 | mg |
| Tensile stress | Yield | ISO527-2/5 | 105 | Mpa |
| Tensile strain | Yield | ISO527-2/5 | 6.0 | % |
| Break | ISO527-2/5 | 60 | % | |
| Tensile modulus | ISO527-2/1 | 3200 | Mpa | |
| Bending modulus | 100mmSpan4 | ASTMD790 | 3520 | Mpa |
| 50.0mmSpan5 | ASTMD790 | 3420 | Mpa | |
| bending strength | Yield,50.0mmSpan5 | ASTMD790 | 174 | Mpa |
| Yield,100mmSpan4 | ASTMD790 | 165 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 60 | % |
| Bending modulus 6 | ISO178 | 3300 | Mpa | |
| Bending strength 6,7 | ISO178 | 160 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 10 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 193 | °C |
| thermal conductivity | ASTMC177 | 0.22 | W/m/K | |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 207 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 199 | °C | |
| RTIElec | UL746 | 170 | °C | |
| Evolution Calendar intelligent importer | UL746 | 170 | °C | |
| RTIStr | UL746 | 170 | °C | |
| Vicat softening temperature | ASTMD152511 | 219 | °C | |
| -- | ISO306/B50 | 211 | °C | |
| -- | ISO306/B120 | 212 | °C | |
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 5.6E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 5E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 5E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 5E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 1.60mm,inAir | ASTMD149 | 33 | KV/mm |
| 1.60mm,in Oil | ASTMD149 | 28 | KV/mm | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 | |
| Dissipation factor | 1kHz | ASTMD150 | 1.3E-03 | |
| 2.45GHz | ASTMD150 | 2.5E-03 | ||
| Dielectric constant | 1kHz | ASTMD150 | 3.15 | |
| Volume resistivity | ASTMD257 | 1E+17 | ohms·cm | |
| Arc resistance 12 | ASTMD495 | PLC5 | ||
| Hot wire ignition | HWI | UL746 | PLC1 | |
| High arc combustion index | HAI | UL746 | PLC3 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC2 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| CharpyNotchedImpact Strength8 | 23°C | ISO179/1eA | 3.0 | kJ/m² |
| Suspended wall beam gap impact strength 9 | -30°C | ISO180/1A | 5.0 | kJ/m² |
| 23°C | ISO180/1A | 5.0 | kJ/m² | |
| ReverseNotchIzodImpact | 3.20mm | ASTMD256 | 1200 | J/m |
| Falling hammer impact | 23°C | ASTMD3029 | 33.9 | J |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 33.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTMD785 | 109 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ASTMD2863 | 44 | % | |
| NBSSmokeDensity-Flaming,Ds,4min | ASTME662 | 2.00 | ||
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| 0.71mm | UL94 | V-2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.