PEI ULTEM™ 1000 GY SABIC INNOVATIVE US

201

Unit Price:
$24242 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced Flame retardant enhance
Application Areas:Electrical field Electronic field Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	Saturation, 23°C	ISO 62	1.3	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.70	%
Molten Volume Flow Rate (MVR)	360°C/5.0 kg	ISO 1133	13.0	cm3/10min
Shrinkage rate - Flow 1		内部方法	0.50 到 0.70	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending stress 2, 3		ISO 178	160	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	内部方法	10.0	mg
Bending modulus 2		ISO 178	3300	Mpa
Tensile stress	Yield	ISO 527-2/50	105	Mpa
Tensile stress	Tensile stress	Break	ISO 527-2/50	85.0	Mpa
Tensile strain	Yield	ISO 527-2/50	6.0	%
Tensile strain	Tensile strain	Break	ISO 527-2/50	60	%
Tensile modulus		ISO 527-2/1	3200	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature	--	ISO 306/A50	215	°C
	Vicat softening temperature	--	ISO 306/B50	211	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	212	°C
Linear coefficient of thermal expansion	Flow : 23 to 150°C	ISO 11359-2	5.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 150°C	ISO 11359-2	5.0E-5	cm/cm/°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
thermal conductivity		ISO 8302	0.24	W/m/K
RTI		UL 746	170	°C
RTI Imp		UL 746	170	°C
RTI Elec		UL 746	170	°C
Hot deformation temperature 6	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	200	°C
Hot deformation temperature 6	Hot deformation temperature 6	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	190	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative permittivity	50 Hz	IEC 60250	2.90
	Relative permittivity	60 Hz	IEC 60250	2.90
	Relative permittivity	Relative permittivity	1 MHz	IEC 60250	2.90
Leakage Trace Index	--	IEC 60112	150	V
Leakage Trace Index	Leakage Trace Index	Solution B	IEC 60112	100	V
Dielectric strength	0.800 mm, in Oil	IEC 60243-1	33	KV/mm
	Dielectric strength	1.60 mm, in Oil	IEC 60243-1	25	KV/mm
	Dielectric strength	Dielectric strength	3.20 mm, in Oil	IEC 60243-1	16	KV/mm
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dissipation factor	50 Hz	IEC 60250	5.0E-4
	Dissipation factor	60 Hz	IEC 60250	5.0E-4
		Dissipation factor	1 MHz	IEC 60250	6.0E-3
		Dissipation factor	Dissipation factor	2.45 GHz	IEC 60250	2.5E-3

injection	Test Result	Unit
drying temperature	150	°C
Suggested maximum moisture content	0.020	%
Processing (melt) temperature	370 到 410	°C
Mold temperature	140 到 180	°C
drying time	4.0 到 6.0	hr
Temperature at the rear of the barrel	340 到 395	°C
Temperature in the middle of the barrel	350 到 405	°C
Temperature at the front of the material cylinder	360 到 415	°C
Spray nozzle temperature	350 到 405	°C
Hopper temperature	80 到 120	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Suspended wall beam gap impact strength 5	-30°C	ISO 180/1A	6.0	kJ/m²
Suspended wall beam gap impact strength 5	Suspended wall beam gap impact strength 5	23°C	ISO 180/1A	6.0	kJ/m²
Unscented Izod Impact Strength 5	-30°C	ISO 180/1U	无断裂
Unscented Izod Impact Strength 5	Unscented Izod Impact Strength 5	23°C	ISO 180/1U	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness	H 358/30	ISO 2039-1	140	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
Burning wire flammability index	3.2 mm	IEC 60695-2-12	960	°C
Extreme Oxygen Index		ISO 4589-2	47	%
UL flame retardant rating	0.40 mm	UL 94	V-2
	UL flame retardant rating	0.75 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.