PEI ULTEM™ HU1000-7HD395 SABIC INNOVATIVE US
90
- Unit Price:
- $10898 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | 24 hr | ASTM D570 | 0.25 | % |
| Saturation, 23°C | ISO 62 | 1.3 | % | |
| Equilibrium, 23°C | ASTM D570 | 1.3 | % | |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.70 | % | |
| Melt Mass-Flow Rate | 337°C/6.6 kg | ASTM D1238 | 9.0 | g/10 min |
| Melt Volume flow Rate | 220°C/5.0 kg | ISO 1133 | 13.0 | cm3/10min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | -- 5, 6 | ISO 178 | 160 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 173 | Mpa | |
| Tensile Strength | Yield 3 | ASTM D638 | 110 | Mpa |
| Yield | ISO 527-2/5 | 105 | Mpa | |
| Break 3 | ASTM D638 | 90.0 | Mpa | |
| Break | ISO 527-2/5 | 85.0 | Mpa | |
| Tensile Modulus | -- 2 | ASTM D638 | 3580 | Mpa |
| -- | ISO 527-2/1 | 3200 | Mpa | |
| Tensile Elongation | Yield 3 | ASTM D638 | 7.0 | % |
| Yield | ISO 527-2/5 | 6.0 | % | |
| Break 3 | ASTM D638 | 60 | % | |
| Break | ISO 527-2/5 | 60 | % | |
| Flexural Modulus | 50.0 mm Span 4 | ASTM D790 | 3430 | Mpa |
| -- 5 | ISO 178 | 3300 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | -- | ASTM D15259 | 218 | °C |
| -- | ISO 306/B50 | 215 | °C | |
| -- | ISO 306/B120 | 211 | °C | |
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 201 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | ISO 75-2/Af | 215 | °C | |
| Linear thermal expansion coefficient | Flow : -20 to 150°C | ASTM E831 | 5.6E-5 | cm/cm/°C |
| Flow : -40 to 40°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C | |
| Across Flow : -20 to 150°C | ASTM E831 | 5.4E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative Tracking Index | UL 746 | PLC 4 | ||
| Hot-wire Ignition | UL 746 | PLC 1 | ||
| High Voltage Arc Tracking Rate | UL 746 | PLC 2 | ||
| High Amp Arc Ignition | UL 746 | PLC 3 | ||
| Arc Resistance | ASTM D495 | PLC 5 | ||
| Dielectric Strength | 1.60 mm, in Air | ASTM D149 | 33 | KV/mm |
| 1.60 mm, in Oil | ASTM D149 | 28 | KV/mm | |
| Dissipation Factor? | 1 kHz | ASTM D150 | 1.3E-3 | |
| 2.45 GHz | ASTM D150 | 2.5E-3 | ||
| Dielectric Constant | 1 kHz | ASTM D150 | 3.15 | |
| Volume Resistivity | ASTM D257 | 1.0E+17 | ohms·cm |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 150 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 350 到 400 | °C | ||
| Mold Temperature | 135 到 165 | °C | ||
| Drying Time | 4.0 到 6.0 | hr | ||
| Suggested Shot Size | 40 到 60 | % | ||
| Rear Temperature | 330 到 400 | °C | ||
| Middle Temperature | 340 到 400 | °C | ||
| Front Temperature | 345 到 400 | °C | ||
| Nozzle Temperature | 345 到 400 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 40 到 70 | rpm | ||
| Vent Depth | 0.025 到 0.076 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 0.00 | J |
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 1300 | J/m |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | ASTM D2863 | 47 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.