PEI ULTEM™ HU1010-7HD395 SABIC INNOVATIVE US

102

Unit Price:
$29056 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Middle flow Biocompatibility Steam sterilization
Application Areas:Medical and nursing suppl Medical devices
Color:--
Grade:Injection grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	Saturation, 23°C	ISO 62	1.3	%
	Water absorption rate	Equilibrium, 23°C	ASTM D570	1.3	%
	Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.70	%
Melt flow rate	337°C/6.6 kg	ASTM D1238	18	g/10 min
Molten Volume Flow Rate (MVR)	360°C/5.0 kg	ISO 1133	25.0	cm3/10min
Shrinkage rate - flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending stress	-- 6, 7	ISO 178	160	Mpa
	Bending stress	Yield, 50.0 mm Span 4	ASTM D790	174	Mpa
	Bending stress	Bending stress	Yield, 100 mm Span 5	ASTM D790	165	Mpa
Tensile strength	Yield 3	ASTM D638	110	Mpa
	Tensile strength	Yield	ISO 527-2/5	105	Mpa
	Tensile strength	Tensile strength	Break 3	ASTM D638	105	Mpa
Tensile modulus	-- 2	ASTM D638	3580	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	3200	Mpa
elongation	Yield 3	ASTM D638	7.0	%
	elongation	Yield	ISO 527-2/5	6.0	%
		elongation	Break 3	ASTM D638	60	%
		elongation	elongation	Break	ISO 527-2/5	60	%
Bending modulus	50.0 mm Span 4	ASTM D790	3420	Mpa
	Bending modulus	100 mm Span 5	ASTM D790	3510	Mpa
	Bending modulus	Bending modulus	-- 6	ISO 178	3300	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg

Thermal performance	Test Condition	Test Method	Test Result	Unit
thermal conductivity		ASTM C177	0.22	W/m/K
RTI		UL 746	170	°C
RTI Imp		UL 746	170	°C
RTI Elec		UL 746	170	°C
Vicat softening temperature	--	ASTM D152510	218	°C
	Vicat softening temperature	--	ISO 306/B50	211	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	212	°C
Linear coefficient of thermal expansion	Flow : -20 to 150°C	ASTM E831	5.6E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	5.0E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	5.0E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	5.0E-5	cm/cm/°C
Thermal deformation temperature under load	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	207	°C
	Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	198	°C
	Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9	ISO 75-2/Af	193	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength	1.60 mm, in Air	ASTM D149	33	KV/mm
Dielectric strength	Dielectric strength	1.60 mm, in Oil	ASTM D149	28	KV/mm
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 4
Hot wire ignition (HWI)		UL 746	PLC 1
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 2
High arc combustion index (HAI) 12		UL 746	PLC 3
Arc resistance 11		ASTM D495	PLC 5
Dissipation factor	1 kHz	ASTM D150	1.3E-3
Dissipation factor	Dissipation factor	2.45 GHz	ASTM D150	2.5E-3
Dielectric constant	1 kHz	ASTM D150	3.15
Volume resistivity		ASTM D257	1.0E+17	ohms·cm

injection	Test Result	Unit
drying temperature	150	°C
Suggested maximum moisture content	0.020	%
Processing (melt) temperature	350 到 400	°C
Mold temperature	135 到 165	°C
drying time	4.0 到 6.0	hr
Suggested injection volume	40 到 60	%
Temperature at the rear of the barrel	330 到 400	°C
Temperature in the middle of the barrel	340 到 400	°C
Temperature at the front of the material cylinder	345 到 400	°C
Spray nozzle temperature	345 到 400	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	40 到 70	rpm
Exhaust hole depth	0.025 到 0.076	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Falling hammer impact	23°C	ASTM D3029	33.0	J
Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	33.0	J
Reverse notch impact	3.20 mm	ASTM D256	1200	J/m
Non notched cantilever beam impact	23°C	ASTM D4812	1300	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ASTM D785	109

flammability	Test Condition	Test Method	Test Result	Unit
Extreme Oxygen Index		ASTM D2863	44	%
UL flame retardant rating	0.71 mm	UL 94	V-2
	UL flame retardant rating	0.75 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.