PEI ULTEM™ 1000-7301 SABIC INNOVATIVE US
204
- Unit Price:
- $22884 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Flame retardant enhance
- Application Areas:Electrical field Electronic field Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 24 hr | ASTM D570 | 0.25 | % |
| Equilibrium, 23°C | ASTM D570 | 1.3 | % | |
| Melt flow rate | 337°C/6.6 kg | ASTM D1238 | 9.0 | g/10 min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation rate 2 | Yield | ASTM D638 | 7.0 | % |
| Break | ASTM D638 | 60 | % | |
| Tensile strength | Yield | ASTM D638 | 110 | Mpa |
| Tensile modulus 1 | ASTM D638 | 3580 | Mpa | |
| Poisson's ratio | ASTM E132 | 0.36 | ||
| Bending modulus | 100 mm Span | ASTM D790 | 3510 | Mpa |
| bending strength | Yield, 100 mm Span | ASTM D790 | 165 | Mpa |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 Wheel | ASTM D1044 | 10.0 | mg |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| thermal conductivity | ASTM C177 | 0.22 | W/m/K | |
| RTI | UL 746 | 170 | °C | |
| RTI Imp | UL 746 | 170 | °C | |
| RTI Elec | UL 746 | 170 | °C | |
| Linear coefficient of thermal expansion | Flow : -20 to 150°C | ASTM E831 | 5.6E-5 | cm/cm/°C |
| Across Flow : -20 to 150°C | ASTM E831 | 5.4E-5 | cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 210 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 201 | °C | |
| Vicat softening temperature | ASTM D15254 | 218 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc resistance 5 | ASTM D495 | PLC 5 | ||
| High arc combustion index (HAI) 6 | UL 746 | PLC 3 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 4 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 1 | ||
| Dielectric strength | 1.60 mm, in Air | ASTM D149 | 33 | KV/mm |
| 1.60 mm, in Oil | ASTM D149 | 28 | KV/mm | |
| 3.20 mm, in Oil | ASTM D149 | 20 | KV/mm | |
| Dielectric constant | 100 Hz | ASTM D150 | 3.15 | |
| 1 kHz | ASTM D150 | 3.15 | ||
| Volume resistivity | ASTM D257 | 1.0E+17 | ohms·cm | |
| Dissipation factor | 100 Hz | ASTM D150 | 1.5E-3 | |
| 1 kHz | ASTM D150 | 1.2E-3 | ||
| 2.45 GHz | ASTM D150 | 2.5E-3 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying time | 4.0 到 6.0 | hr | ||
| Suggested injection volume | 40 到 60 | % | ||
| Temperature at the rear of the barrel | 330 到 400 | °C | ||
| Temperature in the middle of the barrel | 340 到 400 | °C | ||
| Temperature at the front of the material cylinder | 345 到 400 | °C | ||
| Spray nozzle temperature | 345 到 400 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.025 到 0.076 | mm | ||
| drying temperature | 150 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 350 到 400 | °C | ||
| Mold temperature | 135 到 165 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Falling hammer impact | 23°C | ASTM D3029 | 36.0 | J |
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 1300 | J/m |
| Reverse notch impact | 3.20 mm | ASTM D256 | 1300 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTM D785 | 109 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ASTM D2863 | 47 | % | |
| UL flame retardant rating | 0.40 mm | UL 94 | V-2 | |
| 0.75 mm | UL 94 | V-0 | ||
| 3.0 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.