PEI ULTEM™ 2212EPR-1000 SABIC INNOVATIVE US

Unit Price:
$7421 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 3.20 mm	内部方法	0.50 到 0.70	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 mm	内部方法	0.50 到 0.70	%
Melt Mass-Flow Rate	337°C/6.6 kg	ASTM D1238	15	g/10 min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	50.0 mm Span 3	ASTM D790	5510	Mpa
Flexural Modulus	Flexural Modulus	100 mm Span 4	ASTM D790	5100	Mpa
Flexural Strength	Yield, 50.0 mm Span 3	ASTM D790	172	Mpa
Flexural Strength	Flexural Strength	Break, 100 mm Span 4	ASTM D790	172	Mpa
Tensile Strength	Yield	ASTM D638	107	Mpa
Tensile Strength	Tensile Strength	Break	ASTM D638	107	Mpa
Tensile Elongation	Yield	ASTM D638	3.0	%
Tensile Elongation	Tensile Elongation	Break	ASTM D638	3.0	%
Tensile Modulus		ASTM D638	5790	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ASTM D15255	210	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	210	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	212	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	205	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	207	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	3.6E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	7.2E-5	cm/cm/°C
RTI		UL 746	105	°C
RTI Imp		UL 746	105	°C
RTI Elec		UL 746	105	°C

Electrical performance	Test Method	Test Result
Comparative Tracking Index	UL 746	PLC 4
High Amp Arc Ignition	UL 746	PLC 4
Hot-wire Ignition	UL 746	PLC 1
High Voltage Arc Tracking Rate	UL 746	PLC 4
Arc Resistance	ASTM D495	PLC 5

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	23°C	ASTM D4812	480	J/m
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	12.0	J

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.40 mm	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.