PEI ULTEM™ 1010M-1100 SABIC INNOVATIVE US
91
- Unit Price:
- $22884 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan transparent enhance Flame retardant
- Application Areas:Food service sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation, 23°C | ISO 62 | 1.3 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.70 | % | |
| Molten Volume Flow Rate (MVR) | 340°C/5.0 kg | ISO 1133 | 13.0 | cm3/10min |
| Shrinkage rate - Flow 1 | 内部方法 | 0.50 到 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress 2, 3 | ISO 178 | 160 | Mpa | |
| Bending modulus 2 | ISO 178 | 3300 | Mpa | |
| Tensile stress | Yield | ISO 527-2/50 | 105 | Mpa |
| Break | ISO 527-2/50 | 85.0 | Mpa | |
| Tensile strain | Yield | ISO 527-2/50 | 6.0 | % |
| Break | ISO 527-2/50 | 60 | % | |
| Tensile modulus | ISO 527-2/1 | 3200 | Mpa | |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 Wheel | 内部方法 | 10.0 | mg |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ISO 306/A50 | 215 | °C |
| -- | ISO 306/B50 | 211 | °C | |
| -- | ISO 306/B120 | 212 | °C | |
| Ball Pressure Test | 123 to 127°C | IEC 60695-10-2 | 通过 | |
| thermal conductivity | ISO 8302 | 0.21 | W/m/K | |
| RTI | UL 746 | 170 | °C | |
| RTI Imp | UL 746 | 170 | °C | |
| RTI Elec | UL 746 | 170 | °C | |
| Linear coefficient of thermal expansion | Flow : 23 to 150°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C |
| Across Flow : 23 to 150°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C | |
| Hot deformation temperature 5 | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 195 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 190 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 1.60 mm, in Oil | IEC 60243-1 | 28 | KV/mm |
| Surface resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | 1.0E+15 | ohms·cm | |
| Relative permittivity | 50 Hz | IEC 60250 | 2.90 | |
| 60 Hz | IEC 60250 | 2.90 | ||
| 1 MHz | IEC 60250 | 2.90 | ||
| Leakage Trace Index | -- | IEC 60112 | 150 | V |
| Solution B | IEC 60112 | 100 | V | |
| Dissipation factor | 50 Hz | IEC 60250 | 5.0E-4 | |
| 60 Hz | IEC 60250 | 5.0E-4 | ||
| 1 MHz | IEC 60250 | 6.0E-3 | ||
| 2.45 GHz | IEC 60250 | 2.5E-3 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 150 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 370 到 410 | °C | ||
| Mold temperature | 140 到 180 | °C | ||
| drying time | 4.0 到 6.0 | hr | ||
| Temperature at the rear of the barrel | 350 到 400 | °C | ||
| Temperature in the middle of the barrel | 360 到 410 | °C | ||
| Temperature at the front of the material cylinder | 370 到 420 | °C | ||
| Spray nozzle temperature | 360 到 410 | °C | ||
| Hopper temperature | 80 到 120 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam gap impact strength 4 | -30°C | ISO 180/1A | 5.0 | kJ/m² |
| 23°C | ISO 180/1A | 5.0 | kJ/m² | |
| Unscented Izod Impact Strength 4 | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H 358/30 | ISO 2039-1 | 140 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 3.2 mm | IEC 60695-2-12 | 960 | °C |
| Extreme Oxygen Index | ISO 4589-2 | 47 | % | |
| UL flame retardant rating | 0.75 mm | UL 94 | V-0 | |
| 3.0 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.