PEI ULTEM™ 2312-1000 SABIC INNOVATIVE SHANGHAI
94
- Unit Price:
- $17256 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 22.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan enhance
- Application Areas:Electrical tools Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow : 3.20 mm | 内部方法 | 0.30 到 0.40 | % |
| Across Flow : 3.20 mm | 内部方法 | 0.45 到 0.55 | % | |
| Moisture Absorption | 24 hr | ASTM D570 | 0.18 | % |
| Equilibrium, 23°C | ASTM D570 | 0.98 | % | |
| Melt Mass-Flow Rate | 337°C/6.6 kg | ASTM D1238 | 10 | g/10 min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Break | ASTM D638 | 3.5 | % |
| Flexural Modulus | 100 mm Span | ASTM D790 | 6550 | Mpa |
| Flexural Strength | Break, 100 mm Span | ASTM D790 | 179 | Mpa |
| Tensile Modulus | ASTM D638 | 5990 | Mpa | |
| Tensile Strength | Break | ASTM D638 | 103 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 207 | °C |
| Linear thermal expansion coefficient | Flow : -20 to 150°C | ASTM E831 | 2.3E-5 | cm/cm/°C |
| Across Flow : -20 to 150°C | ASTM E831 | 2.7E-5 | cm/cm/°C | |
| RTI | UL 746 | 170 | °C | |
| RTI Imp | UL 746 | 170 | °C | |
| RTI Elec | UL 746 | 170 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc Resistance | ASTM D495 | PLC 7 | ||
| Dielectric Constant | 1 kHz | ASTM D150 | 3.70 | |
| 1 MHz | ASTM D150 | 3.49 | ||
| Comparative Tracking Index | UL 746 | PLC 4 | ||
| Hot-wire Ignition | UL 746 | PLC 1 | ||
| High Amp Arc Ignition | UL 746 | PLC 3 | ||
| High Voltage Arc Tracking Rate | UL 746 | PLC 0 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 150 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 350 到 400 | °C | ||
| Mold Temperature | 135 到 165 | °C | ||
| Drying Time | 4.0 到 6.0 | hr | ||
| Suggested Shot Size | 40 到 60 | % | ||
| Rear Temperature | 330 到 400 | °C | ||
| Middle Temperature | 340 到 400 | °C | ||
| Front Temperature | 345 到 400 | °C | ||
| Nozzle Temperature | 345 到 400 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 40 到 70 | rpm | ||
| Vent Depth | 0.025 到 0.076 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Reverse Notch Izod Impact | 3.20 mm | ASTM D256 | 310 | J/m |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 0.8 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.