Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.70 | % |
| Moisture Absorption | 24hr | ASTMD570 | 0.16 | % |
| Melt Mass-Flow Rate | 337°C/6.6kg | ASTMD1238 | 4.2 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 10.0 | mg |
| Tensile Modulus | | ASTMD638 | 2900 | Mpa |
| Tensile Strength | Yield | ASTMD638 | 100 | Mpa |
| Flexural Modulus | 100mmSpan | ASTMD790 | 3100 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 60 | % |
| Flexural Strength | Yield,100mmSpan | ASTMD790 | 138 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| RTIElec | | UL746 | 160 | °C |
| Evolution Calendar intelligent importer | | UL746 | 160 | °C |
| RTIStr | | UL746 | 160 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 207 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | ASTMD257 | 5.8E+16 | ohms |
| Dielectric Constant | 100Hz | ASTMD150 | 3.12 | |
| Volume Resistivity | | ASTMD257 | 1.1E+17 | ohms·cm |
| Dissipation Factor? | 100Hz | ASTMD150 | 1.7E-03 | |
| Dielectric Strength | 3.20mm,inOil | ASTMD149 | 18 | KV/mm |
| Comparative Tracking Index | CTI | UL746 | PLC4 | |
| Hot-wire Ignition | HWI | UL746 | PLC0 | |
| High Amp Arc Ignition | HAI | UL746 | PLC0 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC3 | |
| Arc Resistance | | ASTMD495 | PLC5 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Reverse Notch Izod Impact | 3.20mm | ASTMD256 | 2100 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 123 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.