PEI ULTEM™ ATX3562R-7301 SABIC INNOVATIVE US
93
- Unit Price:
- $9905 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability High temperature resistan
- Application Areas:Electronic and electrical Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.20to0.30 | % |
| TD：3.20mm | 内部方法 | 0.30to0.50 | % | |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.10 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.040 | % | |
| Melt Mass-Flow Rate | 337°C/6.6kg | ASTMD1238 | 20 | g/10min |
| Melt Volume flow Rate | 360°C/5.0kg | ISO1133 | 20.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ISO527-2/1 | 14700 | Mpa | |
| Tensile Stress | Yield | ISO527-2/5 | 121 | Mpa |
| Break | ISO527-2/5 | 121 | Mpa | |
| Tensile Strain | Yield | ISO527-2/5 | 1.4 | % |
| Break | ISO527-2/5 | 1.4 | % | |
| Tensile Elongation | Yield | ASTMD638 | 2.5 | % |
| Tensile Modulus | ASTMD638 | 14900 | Mpa | |
| Tensile Strength | Yield | ASTMD638 | 125 | Mpa |
| Break | ASTMD638 | 125 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 12900 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 180 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 2.5 | % |
| Flexural Modulus | ISO178 | 13600 | Mpa | |
| Flexural Strength | ISO178 | 172 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 195 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 182 | °C | |
| Linear thermal expansion coefficient | TD：23to150°C | ISO11359-2 | 3.8E-05 | cm/cm/°C |
| MD：-40to150°C | ASTME831 | 1.6E-05 | cm/cm/°C | |
| MD：23to150°C | ISO11359-2 | 1.6E-05 | cm/cm/°C | |
| TD：-40to150°C | ASTME831 | 3.8E-05 | cm/cm/°C | |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 183 | °C |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
| Vicat Softening Temperature | ASTMD152510 | 184 | °C | |
| -- | ISO306/B50 | 187 | °C | |
| -- | ISO306/B120 | 195 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | ASTMD257 | 2.1E+15 | ohms | |
| Volume Resistivity | ASTMD257 | 6E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 12.0 | J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 4.8 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 5.4 | kJ/m² |
| 23°C | ISO180/1A | 5.6 | kJ/m² | |
| Reverse Notch Izod Impact | 3.20mm | ASTMD256 | 110 | J/m |
| UnnotchedIzodImpactStrength8 | 23°C | ISO180/1U | 5.6 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.