PEI ULTEM™ 1010GY5803 SABIC INNOVATIVE US
86
- Unit Price:
- $22451 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan transparent enhance Flame retardant
- Application Areas:Food service sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Saturation, 23°C | ISO 62 | 1.3 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.70 | % | |
| Melt Volume flow Rate | 340°C/5.0 kg | ISO 1133 | 13.0 | cm3/10min |
| Modeling Shrinkage - Flow | 内部方法 | 0.50 到 0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | ISO 178 | 160 | Mpa | |
| Flexural Modulus | ISO 178 | 3300 | Mpa | |
| Tensile Stress | Yield | ISO 527-2/50 | 105 | Mpa |
| Break | ISO 527-2/50 | 85.0 | Mpa | |
| Tensile Strain | Yield | ISO 527-2/50 | 6.0 | % |
| Break | ISO 527-2/50 | 60 | % | |
| Tensile Modulus | ISO 527-2/1 | 3200 | Mpa | |
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 Wheel | 内部方法 | 10.0 | mg |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | -- | ISO 306/A50 | 215 | °C |
| -- | ISO 306/B50 | 211 | °C | |
| -- | ISO 306/B120 | 212 | °C | |
| Ball PressureTest | 123 to 127°C | IEC 60695-10-2 | 通过 | |
| Thermal Conductivity | ISO 8302 | 0.21 | W/m/K | |
| RTI | UL 746 | 170 | °C | |
| RTI Imp | UL 746 | 170 | °C | |
| RTI Elec | UL 746 | 170 | °C | |
| Linear thermal expansion coefficient | Flow : 23 to 150°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C |
| Across Flow : 23 to 150°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C | |
| Heat Deflection Temperature | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 195 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 190 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 1.60 mm, in Oil | IEC 60243-1 | 28 | KV/mm |
| Surface Resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Volume Resistivity | IEC 60093 | 1.0E+15 | ohms·cm | |
| Relative Permittivity | 50 Hz | IEC 60250 | 2.90 | |
| 60 Hz | IEC 60250 | 2.90 | ||
| 1 MHz | IEC 60250 | 2.90 | ||
| Comparative Tracking Index | -- | IEC 60112 | 150 | V |
| Solution B | IEC 60112 | 100 | V | |
| Dissipation Factor? | 50 Hz | IEC 60250 | 5.0E-4 | |
| 60 Hz | IEC 60250 | 5.0E-4 | ||
| 1 MHz | IEC 60250 | 6.0E-3 | ||
| 2.45 GHz | IEC 60250 | 2.5E-3 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 150 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 370 到 410 | °C | ||
| Mold Temperature | 140 到 180 | °C | ||
| Drying Time | 4.0 到 6.0 | hr | ||
| Rear Temperature | 350 到 400 | °C | ||
| Middle Temperature | 360 到 410 | °C | ||
| Front Temperature | 370 到 420 | °C | ||
| Nozzle Temperature | 360 到 410 | °C | ||
| Hopper Temperature | 80 到 120 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO 180/1A | 5.0 | kJ/m² |
| 23°C | ISO 180/1A | 5.0 | kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 140 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glow Wire Flammability Index | 3.2 mm | IEC 60695-2-12 | 960 | °C |
| Oxygen Index | ISO 4589-2 | 47 | % | |
| Flame Rating | 0.75 mm | UL 94 | V-0 | |
| 3.0 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.