PEI ULTEM™ 3452-1000-UA7515 SABIC INNOVATIVE US

Unit Price:
$11031 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	337°C/6.6 kg	ASTM D1238	4.6	g/10 min
Modeling Shrinkage	Flow : 3.20 mm	内部方法	0.15 到 0.25	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 mm	内部方法	0.30 到 0.50	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength	Break	ASTM D638	131	Mpa
Tensile Elongation	Break	ASTM D638	1.4	%
Flexural Modulus	100 mm Span	ASTM D790	12400	Mpa
Flexural Strength	Break, 100 mm Span	ASTM D790	179	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	212	°C
RTI Elec		UL 746	180	°C
RTI Imp		UL 746	180	°C
RTI		UL 746	180	°C

Electrical performance	Test Method	Test Result
Arc Resistance	ASTM D495	PLC 5
Comparative Tracking Index	UL 746	PLC 4
High Amp Arc Ignition	UL 746	PLC 4
High Voltage Arc Tracking Rate	UL 746	PLC 4
Hot-wire Ignition	UL 746	PLC 1

Injection	Test Result	Unit
Drying Temperature	150	°C
Drying Time	4.0 到 6.0	hr
Suggested Max Moisture	0.020	%
Suggested Shot Size	40 到 60	%
Rear Temperature	330 到 400	°C
Middle Temperature	340 到 400	°C
Front Temperature	345 到 400	°C
Nozzle Temperature	345 到 400	°C
Processing (Melt) Temp	350 到 400	°C
Mold Temperature	135 到 165	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Reverse Notch Izod Impact	3.20 mm	ASTM D256	220	J/m

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.77 mm	UL 94	V-0
Flame Rating	Flame Rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.