Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.20to0.40 | % |
Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.20to0.40 | % |
Moisture Absorption | 24hr | ASTMD570 | 0.16 | % |
Moisture Absorption | Equilibrium,23°C | ASTMD570 | 0.90 | % |
Melt Mass-Flow Rate | 337°C/6.6kg | ASTMD1238 | 5.0 | g/10min |
Density / Specific Gravity | | ASTMD792 | 1.51 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Strength | Break,100mmSpan | ASTMD790 | 228 | Mpa |
Tensile Modulus | | ASTMD638 | 9310 | Mpa |
Tensile Strength | Yield | ASTMD638 | 169 | Mpa |
Tensile Strength | Break | ASTMD638 | 159 | Mpa |
Flexural Modulus | 100mmSpan | ASTMD790 | 8960 | Mpa |
Tensile Elongation | Break | ASTMD638 | 3.0 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD:-20to150°C | ASTME831 | 2E-05 | cm/cm/°C |
Vicat Softening Temperature | | ASTMD15255 | 228 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 212 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 210 | °C |
RTIElec | | UL746 | 180 | °C |
Evolution Calendar intelligent importer | | UL746 | 170 | °C |
RTIStr | | UL746 | 180 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 1kHz | ASTMD150 | 1.5E-03 | |
Dissipation Factor? | 2.45GHz | ASTMD150 | 5.3E-03 | |
Dielectric Constant | 1kHz | ASTMD150 | 3.70 | |
Volume Resistivity | | ASTMD257 | 3E+16 | ohms·cm |
Comparative Tracking Index | CTI | UL746 | PLC4 | |
Arc Resistance | | ASTMD495 | PLC6 | |
High Amp Arc Ignition | HAI | UL746 | PLC4 | |
High Voltage Arc Tracking Rate | HVTR | UL746 | PLC3 | |
Dielectric Strength | 1.60mm,inAir | ASTMD149 | 25 | KV/mm |
Dielectric Strength | 1.60mm,in Oil | ASTMD149 | 30 | KV/mm |
Hot-wire Ignition | HWI | UL746 | PLC1 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Reverse Notch Izod Impact | 3.20mm | ASTMD256 | 490 | J/m |
Notched Izod Impact Strength | 23°C | ASTMD256 | 85 | J/m |
Notched Izod Impact Strength | 23°C | ASTMD4812 | 430 | J/m |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Scale | ASTMD785 | 114 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | ASTMD2863 | 50 | % |
UL flame retardant rating | 0.25mm | UL94 | V-0 | |
UL flame retardant rating | 1.2mm | UL94 | 5VA | |
NBSSmokeDensity-Flaming,Ds,4min | | ASTME662 | 1.60 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.