PEEK LNP™ THERMOCOMP™ LC006EX1-BKNAT SABIC INNOVATIVE NANSHA
85
- Unit Price:
- $72421 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：24hr | ASTMD955 | 0.10 | % |
| TD：24hr | ASTMD955 | 0.40 | % | |
| TD:24hr | ISO294-4 | 0.40 | % | |
| MD:24hr | ISO294-4 | 0.12 | % | |
| Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.080 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.070 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Break | ISO527-2 | 230 | Mpa |
| Tensile Strain | Break | ISO527-2 | 1.5 | % |
| Flexural Stress | ISO178 | 347 | Mpa | |
| Coefficient of Friction | Dynamic | ASTMD3702Modified | 0.30 | |
| Static | ASTMD3702Modified | 0.32 | ||
| Tensile Modulus | ASTMD638 | 30800 | Mpa | |
| Tensile Modulus | ISO527-2/1 | 24700 | Mpa | |
| Tensile Elongation | Break | ASTMD638 | 1.5 | % |
| Flexural Modulus | ASTMD790 | 20200 | Mpa | |
| ISO178 | 24300 | Mpa | ||
| Flexural Strength | ASTMD790 | 325 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 226 | Mpa |
| Specific Wear Rate | ASTMD3702Modified | 55.0 | 10^-10in^5-min/ft-lb-hr |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | >240 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | >240 | °C | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | >299 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | >299 | °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 1.2E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 1.2E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 2.9E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 2.9E-05 | cm/cm/°C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 7.8 | kJ/m² |
| UnnotchedIzodImpactStrength3 | 23°C | ISO180/1U | 43 | kJ/m² |
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 12.5 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 0.77mm,TestingbySABIC | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.