PEEK VICTREX® 90GL30 VICTREX UK

Unit Price:
$73971 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
SpiralFlow4	--5	内部方法	18.5	CM
SpiralFlow4	SpiralFlow4	--6	内部方法	22.0	CM
Shrinkage rate 7	TD	ISO294-4	0.90	%
Shrinkage rate 7	Shrinkage rate 7	MD	ISO294-4	0.30	%
Water absorption rate	Saturation,23°C	ISO62	0.30	%
Water absorption rate - saturation	100°C	ISO62	0.450	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ISO527-2	12000	Mpa
Bending stress	275°C	ISO178	75.0	Mpa
Compressive stress	23°C	ISO604	250	Mpa
	Compressive stress	120°C	ISO604	160	Mpa
	Compressive stress	Compressive stress	250°C	ISO604	55.0	Mpa
Tensile stress	Break,23°C	ISO527-2	195	Mpa
	Tensile stress	Break,125°C	ISO527-2	130	Mpa
		Tensile stress	Break,175°C	ISO527-2	80.0	Mpa
			Tensile stress	Break,225°C	ISO527-2	60.0	Mpa
			Tensile stress	Tensile stress	Break,275°C	ISO527-2	45.0	Mpa
Tensile strain	Break,23°C	ISO527-2	2.4	%
Bending modulus	23°C	ISO178	11500	Mpa
Bending stress	23°C	ISO178	290	Mpa
	Bending stress	125°C	ISO178	230	Mpa
	Bending stress	Bending stress	175°C	ISO178	115	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
thermal conductivity	23°C10	ISO22007-4	0.35	W/m/K
Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/Af	335	°C
Glass transition temperature 8		ISO11357	143	°C
Melting temperature		ISO11357-3	343	°C
Linear coefficient of thermal expansion	MD:<143°C	ISO11359-2	2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD:>143°C	ISO11359-2	2E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD:<143°C	ISO11359-2	4.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:>143°C	ISO11359-2	1.1E-04	cm/cm/°C
thermal conductivity	23°C9	ISO22007-4	0.30	W/m/K

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC60093	1E+16	ohms·cm
Dielectric strength	2.00mm	IEC60243-1	23	KV/mm
Dielectric constant	23°C,1kHz	IEC60250	3.30
Dissipation factor	23°C,1MHz	IEC60250	4E-03
Leakage Trace Index		IEC60112	150	V

Filling analysis	Test Condition	Test Method	Test Result	Unit
Melt viscosity	400°C	ISO11443	200	Pa·s

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179/1U	45	kJ/m²
Unscented Izod impact strength	23°C	ISO180	45	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Shore hardness	Shore D,23°C	ISO868	87

flammability	Test Condition	Test Method	Test Result	Unit
Burning wire flammability index	2.0mm	IEC60695-2-12	960	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.