Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
SpiralFlow3,4 | | 内部方法 | 13.0 | CM |
Modeling Shrinkage | TD | ISO294-4 | 1.7 | % |
Modeling Shrinkage | MD | ISO294-4 | 1.2 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Compressive Stress | 23°C | ISO604 | 105 | Mpa |
Compressive Stress | 120°C | ISO604 | 65.0 | Mpa |
Tensile Modulus | 23°C | ISO527-2 | 3200 | Mpa |
Flexural Modulus | 23°C | ISO178 | 3200 | Mpa |
Flexural Stress | 23°C6 | ISO178 | 125 | Mpa |
Flexural Stress | 3.5%Strain,23°C | ISO178 | 100 | Mpa |
Flexural Stress | 125°C | ISO178 | 70.0 | Mpa |
Flexural Stress | 175°C | ISO178 | 18.0 | Mpa |
Flexural Stress | 275°C | ISO178 | 13.0 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2 | 78.0 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 25 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Glass Transition Temperature | --7 | ISO11357-2 | 143 | °C |
Glass Transition Temperature | --8 | ISO11357-2 | 150 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/Af | 150 | °C |
Linear thermal expansion coefficient | MD:<143°C | ISO11359-2 | 4E-05 | cm/cm/°C |
Linear thermal expansion coefficient | MD:>143°C | ISO11359-2 | 1.2E-04 | cm/cm/°C |
Linear thermal expansion coefficient | TD:<143°C | ISO11359-2 | 6E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:>143°C | ISO11359-2 | 1.4E-04 | cm/cm/°C |
Melting temperature | | ISO11357-3 | 343 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Constant | 23°C,1kHz | IEC60250 | 2.80 | |
Volume Resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
Dielectric Strength | 2.00mm | IEC60243-1 | 26 | KV/mm |
Dissipation Factor? | 23°C,1MHz | IEC60250 | 4E-03 | |
Comparative Tracking Index | | IEC60112 | 150 | V |
Fill Analysis | Test Condition | Test Method | Test Result | Unit |
---|
Melt Viscosity | 400°C | ISO11443 | 350 | Pa·s |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod impact strength | 23°C | ISO180 | 无断裂 | |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 无断裂 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore D,23°C | ISO868 | 81 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.